热轧型钢轧辊的断裂行为分析及对策
|
|
英文标题：Analysis and countermeasure for fracture forms of rolls in hot rolling section steel |
|
作者：吴成军 |
|
单位：宝钢股份特殊钢分公司 上海200940 |
|
关键词：型钢 轧辊 断裂 |
|
分类号：TG333.17 |
|
出版年,卷(期):页码：2007,32(1):97-99 |
|
摘要：
|
|
热轧型钢过程中经常发生轧辊断裂现象,断裂部位主要在轧辊的孔型处、辊颈处及辊颈与辊身交界处。分析了轧辊产生断裂的原因,认为断辊主要是由轧辊材质热处理回火不充分或存在铸造缺陷、轧辊冷却不良及轧制操作不当引起的,并从技术和管理两个方面提出了相应的控制措施。
|
|
Roll fracture often takes place in hot rolling section steel.The fracture position is mainly located at the roll caliber,roll neck and boundary between the roll neck and roll body.The causes of rolls fracture are analysed.The fracture of rolls results from inadequate heat treatment temper of rolls or existing foundry defects in rolls,ill roll cooling and improper operation during rolling.Meanwhile,the corresponding measures from the aspects of technology and management are put forward.
|
|
基金项目：
|
|
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]高明杰.结合生产实际谈降低轧辊消耗[J].河北冶金,1998,(2~5):153 155.
[2]商存量,刘微.中厚板轧机轧辊断裂原因分析[J].轧钢,2002,19(2):31 32.
[3]陈联满.轧辊辊颈断裂分析[J].理化检验-物理分册,2001,37(7):305 308.
[4]张维,李建民.轧辊断裂原因分析[J].山东冶金,1999(增刊):124 126.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|