研究了C194合金变形与固溶时效热处理工艺条件对其组织性能的影响。研究结果表明:热轧的C194合金,经过850℃固溶、500℃时效处理及二次冷变形后,材料具有较高的力学性能和导电性能,经检测合金材料的抗拉强度达538.5MPa,电导率为81.8%IACS。
|
|
This paper is about construction and characteristics of C194,which are effected by heat-treatment of solution and aging.The result shows that with the solution temperature of 850℃ and aging temperature of 500℃ and two times cold rolling,the strip has a quite good mechanical features and electric conductivity.The tensile strength of strip is 538.5 MPa,and the electric conductivity is 81.8%IACS.
|
|
基金项目：
|
|
江西省自然基金资助项目(550033)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]赵谢群.引线框架铜合金材料研究及开发进展[J].稀有金属,2003,27(6):777 781.
[2]王涛,王碧文.IC铜合金引线框架材料[J].有色金属加工,2002,31(2):9 17.
[3]Ryu H J,Baik H.K.Effect of thermo-mechanical treatmenton microstructure and properties of Cu-base lead fframe alloy[J].Journal of Materials Science,2000,35:3641 3646
[4]马莒生,黄福祥,黄乐,等.铜基引线框架材料的研究与发展[J].功能材料,2002,33(1):1 3.
[5]涂思京,闫晓东,谢水生,等.引线框架用铜合金C194的组织性能研究[J].稀有金属,2004,28(1):199 201.
[6](日)Noriyuki Nomoto.具有高导电和优良耐热性的铜铁合金C194 ESH的生产方法[J].铜加工,2003,1:20 25.
[7]袁振宇,董企铭.时效对Cu Fe P合金显微硬度及导电率的影响[J].热加工工艺,2002,3:33 34.
[8]曹育文,马莒生,王碧文,等.QFe2.5型引线框架用铜合金热处理工艺研究[J].金属热处理学报,1998,19(4):32 37.
[9]刘勇,陆德平,杨湘杰,等.热处理工艺对Cu Fe P合金显微硬度及导电率的影响[J].金属热处理,2004,29(5):35 37.
[10]陈彬,董企铭,康布喜,等.热轧态Cu Fe P合金的相变动力学研究[J].热加工工艺,2003,(6):9 12.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|