镁基复合材料真空吸渗挤压成形质量控制与缺陷预防

英文标题：Quality control and defect prevention of magnesium matrix composites by extrusion directly following vacuum infiltration

作者：刘健齐乐华关俊涛周计明

单位：西北工业大学机电学院

关键词：镁基复合材料真空吸渗挤压缺陷预防

分类号：TG376

出版年,卷(期):页码：2010,35(2):75-78

摘要：

研究镁基复合材料真空吸渗挤压工艺参数对制件成形质量的影响规律以及参数选取原则,对成形过程中典型成形缺陷的主要特征、成因等进行了分析,提出了针对性的预防和控制措施:提高液态金属浇注温度与模具预热温度,可以改善预制体的浸渗效果;严格控制挤压温度是预防表面裂纹的根本措施;改善模具表面质量或润滑状况,可以降低表面裂纹及制件弯曲产生的几率。

The influence of process parameters on the forming quality of magnesium matrix composites by extrusion directly following vacuum infiltration was studied,and the selection method of process parameters was put forward.The main characteristics and causes of typical defects were analyzed,and the prevention and control measures were proposed,which means that higher pouring temperature and preheating temperature of mould can contribute to perfecting the infiltration of magnesium liquid in the preformed body.It is the key measure that extrusion temperature should be strickly controlled to prevent the occurrence of surface cracks.Improving the surface quality and lubrication state of mould can reduce the probability of surface cracking and workpiece bending.

基金项目：

国家自然科学基资助项目(50575185)

参考文献：

[1]齐乐华,苏力争,欧阳海波,等.一体化镁基复合材料制备装置及方法[P].中国,200810017359.4.
[2]Shiomi M,Takano D,Osakada K,et al.Forming of alumin-ium alloy at temperatures just below melting point[J].In-ternational Journal of Machine Tools and Manufacture,2003,43(3):229-235.
[3]Duan X J,Velay X,Sheppard T.Application of finite ele-ment method in the hot extrusion of aluminium alloys[J].Materials Science and Engineering,2004,A369:66-75.
[4]张艳秋,徐福昌,王冠,等.复杂盘饼类铝合金锻件等温成形缺陷分析[J].锻压技术,2008,33(05):10-13.
[5]姜巨福,罗守,王迎,等.SiCp/2024复合材料棒材半固态挤压数值模拟[J].特种铸造及有色合金,2003,(增刊):253-258.
[6]Li Z J,Fei W D,Yue H Y,et al.Hot deformation behaviorsof Bi2O3-coated Al18B4O33 whisker reinforced aluminum ma-trix composite with high formability[J].Composites Scienceand Technology,2007,67(6):963-973.
[7]Rahmani Fard R,Akhlaghi F.Effect of extrusion tempera-ture on the microstructure and porosity of A356-SiCpcompos-ites[J].Journal of Materials Processing Technology,2007,187-188:433-436.
[8]Qi L H,Zhou J M,Su L Z,et al.Fabrication of Csf/Mgcomposites using extrusion directly following vacuum infiltra-tion-Part 2:Forming process study[J].Solid State Phenome-na,2008,141-143:91-96.
[9]Ouyang H B,Li H J,Qi L H,et al.Fabrication of short car-bon fiber preforms coated with pyrocarbon/SiC for liquid met-al infiltration[J].Journal of Materials Science,2008,43(13):4618-4624.

服务与反馈：

【文章下载】【加入收藏】