电爆炸喷涂技术用于模具表面强化的研究

英文标题：Research on electrical explosion coating technology used for die surface consolidation

作者：杨新海计亚平许岚冯泽舟陆辛

关键词：电爆炸喷涂 2Cr13合金模具表面强化

分类号：TG386

出版年,卷(期):页码：2010,35(5):127-129

摘要：

采用电爆炸喷涂技术，将商用材料2Cr13喷涂在生物质能材料固化颗粒成形模具表面，通过对涂层进行扫描电镜、能谱分析、强度试验可知， 2Cr13经电爆炸喷涂技术在模具表面形成的涂层致密、无微裂纹、空洞较少、合金元素烧损少、与基体结合强度高。将这种经电爆炸喷涂强化后的生物质颗粒成形模具用于生产考核，寿命可提高一倍。试验与生产考核的结果为人们采用“普通钢+电爆炸喷涂表面强化”工艺代替用昂贵的模具钢来制作模具提供了依据。

The electrical explosion coating technology was used for the surface consolidation of the die, the material of the coating was 2Cr13. The coating was detected and analyzed by scanning electron microscopy, energy dispersive spectroscopy and strength test. The results show that the coatings are dense with no micro-cracks, less cavity and alloy element losses and the coating and substrate has a high bonding strength. The mold strengthened by biomass particles forming after the electrical explosion spraying 2Cr13 was examined in production.Its life can be doubled.The experimental and production result provide the basis for adopting “ordinary steel + electric explosion spraying surface hardening process” instead of making the mould with the expensive mold steel.

基金项目：

浙江省科学技术厅重大机电装备专项（2007C11035）

参考文献：

［1］谢嘉生，徐妍娜，丘宏扬，等.提高模具使用寿命的表面强化新技术[J].锻压机械，2000，（3）：37-39.
［2］李月恩，赵军，王维.热作模具表面失效与模具寿命关系研究[J].锻压技术,2009,34(2):91-93.
［3］李柯,胡自化,潘韧坚.耐磨堆焊技术在模具表面强化中的应用[J].模具制造,2003,9(26):54-56.
［4］艾明平，来克娴.5CrNiMo热锻模具堆焊修复工艺研究[J].锻压技术,2009,34(4):114-116.
［5］于琳华,殷秋菊,林东玲.表面强化技术在模具中的应用与发展[J].热处理技术与装备,2009,30(2):5-8.
［6］高玉魁.模具的表面强化与涂层改性工艺技术[J].金属加工，2009，（9）:17-19.
［7］刘宗德，杨昆，段鹏，等.线爆炸法制备WC-Co硬质合金涂层的实验研究[J].爆炸与冲击,2003,23(2)：116-121.
［8］马忠云, 刘宗德, 徐亮, 等.电爆炸喷涂技术在440t/h CFB锅炉上防磨的应用[J].节能技术，2005，23（5）：405-408.
［9］蒲泽林，刘宗德,陆辛，等.电热定向爆炸制备高速钢涂层的试验研究[J].金属热处理，2004，29（10）：36-38.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】