新型热作模具钢在气门精锻模上的应用

英文标题：New hot forging die steel application in valve precision forging die

作者：金康陈东褚作明邓剑雄

关键词：热精锻模模具钢模具寿命热处理

分类号：TG76

出版年,卷(期):页码：2011,36(1):103-108

摘要：

分析了气门精锻模具的工况条件及失效特点，研究了新型热作模具钢（RJD钢）的实验性能、热处理工艺及其在气门精锻模具上的生产应用。实验表明，RJD钢抗氧化性及热稳定性优于H13、8407钢，经1120 ℃淬火、620 ℃ 回火后硬度为53 HRC左右，RJD钢性能符合气门精锻模服役的工况条件要求。生产应用表明，RJD钢具有更突出的强韧性能，使用寿命显著高于3Cr2W8V、4Cr5MoSiV1钢，能很好满足气门热精锻成形模具的使用要求。

The working conditions and the failure characteristics of the valve precision forging die were analyzed, and the new hot working die steel's experimental performance, technology for heating processing and application in the valve precision forging die were also discussed. The results show that the oxidation-resistance and heat stability of RJD steel are better than those of H13 and 8407 steel with hardness of about 53HRC after quenching at 1120 ℃ and tempering at 620 ℃. The performance of RJD steel meets the requirement of the valve precision forging die's working condition. The productive application shows that RJD steel has more outstanding strength and toughness behaviors and its service life is significantly longer than 3Cr2W8V and 4Cr5MoSiV1，which can sufficiently meet the requirement of the valve precision forging die.

基金项目：

“高档数控机床与基础制造装备”科技重大专项-“大型精密模具-大型、复杂、高寿命压铸模具”子项目（2009ZX04013-033-01）

参考文献：

［1］潘振鹏,黄惠平,谢光荣,等.气门热锻模失效分析及HD2钢的应用[J].模具工业,1998，(7):44-46.
［2］李芬,潘振鹏,王桂棠,等.012Al钢在气门热精锻模具的应用[J].锻压技术,1997，22(3):60-64.
［3］李月恩，赵军，王维.热作模具表面失效与模具寿命关系研究[J].锻压技术,2009，34（2）:91-93.
［4］李乾方.气门锻模的失效分析及提高寿命措施的探讨[J].内燃机,2003，(3):19-20.
［5］宁志坚,章争荣,孙友松,等.气门毛坯终锻模具的失效分析与对策[J].材料研究与应用,2009，(3):100-102.
［6］章争荣,黄丹娜,莫东强.气门毛坯局部镦挤终锻成形工艺研究[J].锻压技术，2009，34(5):1-4.
［7］蔡莲淑,石钟良, 潘振鹏,等.组合式气门锻模非正常开裂失效分析[J].金属热处理,2001，(6):32-34.
［8］许珞萍,吴晓春, 邵光杰,等.4Cr5MnSiV1,8407钢的热疲劳性能[A].全国第七届热疲劳学术会议论文集[C].海口，2000.
［9］徐进,陈再枝.模具材料应用手册[M].北京:机械工业出版社,2004.
［10］王孟,刘宗德,宝志坚.H13钢汽车热锻模具失效机理分析[J].锻压技术,2008,33（4）:110-112.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】