典型壳体件热模锻模具开裂分析

英文标题：Analysis of hot forging mould cracking for typcal shell

作者：陈瑞钢赵顺峰周俊

单位：无锡透平叶片有限公司

分类号：TG76

出版年,卷(期):页码：2011,36(5):117-121

摘要：

通过对典型壳体件工艺分析、产品图与锻件图转换、模具设计原则以及生产过程的阐述，研究了影响壳体件热模锻模具开裂失效的几个因素。壳体件模锻应避免出现变形死区以及出现闭式锻造，工艺上应解决坯料中心与模具中心定位问题，锻件设计上注意连皮设计对成形力的影响。分析结果对今后壳体件热模锻工艺制定、锻件设计以及模具结构设计具有十分重要的借鉴意义。

Effects on the hot forging mould cracking of typical shell were studied through analyzing the process of the typical shell, switching between product drawing and forging drawing and the description of design principles and manufacturing process. In order to avoid closed-die forging and deformstion dead areas of the shell, the problem of center location between the blank center and the die center should be solved and the effect of the flash design on the forming force should be cared during the forging design. It provides a significant reference for hot forging mould process design, forging design and die structure design of titanium alloys shell.

基金项目：

参考文献：

[1]洪慎章.锻造实用数据速查手册[M].北京:机械工业出版社,2007.

[2]贺冠雄，赵恒义.壳体等温模锻成形工艺[J].热加工工艺,2003，(2):65.

[3]赵一平.提高热模锻生产中的模具使用寿命[J].锻压技术,2000,25(6):43-47.

[4]方泉水，辛选荣，刘汀.6061铝合金花键壳体冷挤压工艺研究[J].锻压技术,2007,32(1):24-27.

[5]伍太宾，孔凡新，赵治国.2A12铝合金薄壁壳体的近净成形加工技术研究[J].锻压技术,2009,34(4)：105-109.

服务与反馈：

【文章下载】【加入收藏】