采用半固态加工方法制备B4C/Y112复合材料的研究

英文标题：Study on preparation of B4C/Y112 composites by semi-solid processing method

作者：闫洪胡望杰贺儒周冰锋李勇

单位：南昌大学江西理工大学

关键词：半固态 B4C Y112 机械搅拌

分类号：TG146

出版年,卷(期):页码：2011,36(5):128-132

摘要：

通过自行研制开发的新型复合材料半固态连续机械搅拌设备, 制备了半固态的B4C/Y112复合材料浆料, 研究了外加增强颗粒B4C的预热处理、颗粒尺寸和质量分数对半固态固相组织的变化规律，并对制备的含不同质量分数B4C颗粒（颗粒尺寸5~7μm）的复合材料进行拉伸、硬度等力学性能测试。结果表明：B4C颗粒经预热处理，颗粒尺寸越大，质量分数越大，固相颗粒越细小、均匀、圆整。加入经过400 ℃预热处理2h、颗粒尺寸5~7μm和质量分数为6%的B4C颗粒制备的半固态固相颗粒细小、均匀、圆整。半固态铝基复合材料的硬度随着加入B4C颗粒的质量分数增加而不断增大，12 wt.%~B4C/Y112复合材料硬度值最高，达到136HV；其抗拉强度随着B4C含量的增加呈先上升后下降趋势。

Using the self-developed mechanical stirring machine for preparing continuous semi-solid slurry of composites，semi-solid slurry of composites B4C/Y112 was prepared. The effects of some parameters including preheating treatment of B4C particles, different size of B4C particles and different mass fraction of B4C particles on the micro structural evolution in the slurry were described. Then the tensile, hardness and other mechanical properties of materials prepared with different mass fraction of B4C particles（particle size 57μm）were tested. The results show that after preheating treatment of B4C particles, increasing in size and mass fraction of B4C particles, grain in the slurry becomes fine, uniform and round, but the solid fraction reduces. Under the condition of appropriate parameters: 400 ℃ preheating treatment for 2 hours, 57μm size and 6% mass fraction of B4C particles, grain in the slurry becomes fine uniform and round. The hardness of semi\|solid aluminum matrix composites increased with the increasing of concentration of B4C particles, 12wt.%B4C/Y112 composite had the highest hardness, reached to 136HV. With increasing of the mass fraction of B4C particles, its tensile strength increased first and then decreased.

基金项目：

国家自然科学基金(51165032);江西省高等学校科技创新团队计划项目（00008713）；江西省教育厅资助项目（GJJ11269）

参考文献：

[1]孙亦,陈振华.半固态金属基复合材料的制备及流变性研究进展[J].材料导报，2005, 19(3):56-59.

[2]冯小明,张崇才. 复合材料[M]. 重庆：重庆大学出版社,2007.

[3]Haghayeghi R, Zoqui E J, Halvaee A, et al. An investigation on semi-solid Al-7Si-0.3Mg alloy produced by mechanical stirring[J]. Journal of Materials Processing Technology，2005, 169:382-387.

[4]Flemlngs M C. Behavior of metal alloys in the semisolid state[J]. Metal Trans.，1991, 22A(4)：957-981.

[5]Zhang Hongwei, Lin Geng, Lina Guan, et al. Effects of SiC particle pretreatment and stirring parameters on the microstructure and mechanical properties of SiCp/Al\|6.8 Mg composites fabricated by semi-solid stirring technique[J]. Materials Science and Engineering A.，2010, 528: 513-518.

[6]杜之明,张晓华,罗守靖.双螺杆制备半固态坯料装置的设计[J].锻压技术,2009,34(4):86-89.

[7]周冰锋,闫洪,王涛. 机械搅拌法制备半固态铝合金的研究[J]. 特种铸造及有色合金,2009,29(7):625-628.

[8]徐跃,康永林,王朝辉.机械搅拌制备半固态浆料固相颗粒形貌的研究[J].特种铸造及有色合金,2006,26(1):36-38.

[9]王东山,薛向欣,刘然,等.B4C/ Al 复合材料的研究进展及展望[J]. 材料导报,2007,(21):388-390.

[10]彭可武,马贺利, 陈韧,等. B4C/Al复合材料的相及其显微组织的研究[J]. 热加工工艺,2010,39(12):96-98.

服务与反馈：

【文章下载】【加入收藏】