板料成形过程中成形速度对B340/590DP摩擦性能的影响

英文标题：Influence of forming speed on friction property of B340/590DP in sheet metal forming

作者：刘倩李建军付秀娟黄亮

单位：华中科技大学

关键词：板料成形成形速度摩擦性能

分类号：TG30

出版年,卷(期):页码：2012,37(5):27-30

摘要：

基于伺服压力机技术，采用板料滑动拉伸摩擦试验，研究了在板料成形过程中成形速度对B340/590DP板料摩擦性能的影响，分析了成形速度对摩擦性能的作用机理。结果表明，板料初始成形速度越小，初始摩擦力越小；速度变化瞬间摩擦力急剧变化，然后逐渐稳定；前后成形速度设置相差越大，摩擦力变化越大。因此，为了获得良好的成形性能和加工效率，可以选取较小的初始成形速度，保证较小的摩擦力以利于材料的塑性流动，然后采用较大的后续成形速度以保证加工效率。

Based on servo press technology and flat sliding tensile friction test, the influence of forming speed on friction property and the frictional mechanism of B340/590DP in sheet metal forming were studied. Test results show that the smaller initial forming speed is at the beginning, the smaller initial frictional force is; the frictional force changes sharply when forming speed changes instantly, and then tends to be stable; the more discrepancy of the forming speed between former stage and later stage is, the more greatly the frictional force changes. Consequently, the less initial forming speed was chosen to decrease the frictional force in favor of plastic flow in order to obtain the good forming performance, and then the more succeeding forming speed was chosen to obtain high efficiency.

基金项目：

国家自然科学基金资助项目（50975108，51105042）；国家科技重大专项资助课题(2011ZX04016051)

参考文献：

［1］Lee B H, Keum Y T, Wagoner R H. Modeling of the friction caused by lubrication and surface roughness in sheet metal forming [J]. Journal of Materials Processing Technology, 2002, 130131: 60-63.
［2］Hongying Gong, Zhonling Lou, Zhiling Zhang. Studies on the friction and lubrication characteristics in the sheet steel drawing process [J]. Journal of Materials Processing Technology, 2004, 151(13): 328-333.
［3］Serhat Kaya, Giovanni Spampinato, Taylan Altan. An experimental study on nonisothermal deep drawing process using aluminum and magnesium alloys [J]. Journal of Manufacturing Science and Engineering, 2008, 130(6): 1-11.
［4］李建.伺服压力机发展及其应用[J]. 一重技术, 2010, (5): 1-5.
［5］闵建成, 闫长海, 祁长洲,等. 伺服压力机的特点与应用[J].金属加工, 2010, (23): 6-10.
［6］孙友松, 周先辉, 黎勉, 等. 交流伺服压力机及其关键技术[J]. 锻压技术, 2008, 33(4): 1-8.
［7］常琛扬, 翟敬梅, 夏琴香, 等. 基于伺服压力机的凸缘筒形件拉深成形数值分析[J].锻压技术, 2011, 36(4): 59-63.
［8］Kozo Osakada. Application of servo presses to metal forming processes[A]. Proceedings of the 13th International Conference on Metal Forming [C]. Japan: Mori K, 2010.
［9］甄舒. B340/590DP电阻点焊接头组织与力学性能的研究[D]. 长春: 吉林大学, 2010.
［10］赵振铎, 许洪民, 张志红, 等. 金属板料塑性成形摩擦机理的力学模型探讨[J]. 塑性工程学报, 2003, 10(1): 52-56.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】