功率超声制备A356半固态浆料及流变模锻研究

英文标题：Research on A356 semi-solid slurry prepared by power ultrasound and rheological die forging

作者：姜丽红刘昭亮王家宣李超邱泽廷

关键词：功率超声半固态流变模锻力学性能

分类号：TG249.9；TG376.1

出版年,卷(期):页码：2012,37(5):56-59

摘要：

试验采用功率超声双振动头装置制备出球化的非枝晶A356半固态浆料，随即将浆料用于流变模锻。通过对比锻件不同位置的金相组织，发现锻件上、下两端的晶粒较细小，中间部分的晶粒较粗大且液相少。分析了半固态浆料在压力条件下的浆料内部的运动过程。研究了在640℃浇注温度下，经过功率超声处理与未经过超声处理的锻件力学性能，发现经过超声处理的浆料进行模锻所得的锻件力学性能更优。

Spheroidization and non dendritic A356 semi-solid slurry was prepared using power ultrasonic double vibration heads device, then the slurry was used in rheological die forging. The different positions of forgings metallographic structure were compared. The results show that the grains of upper and bottom are small; the grain of central part is coarse where the liquid phase is less than margin. The internal motion process of semi-solid slurry under the condition of the pressure was analyzed. The forgings mechanical performances at pouring temperature of 640 ℃ with and without power ultrasound treated were studied, which show that the treated one is better.

基金项目：

中航一集团“材料热加工技术”航空科技重点实验室开放基金资助项目（ZK200801003）

参考文献：

［1］赵祖德,罗守靖.轻合金半固态成形技术[M].北京:化学工业出版社,2007.
［2］郭洪民.半固态铝合金流变成形工艺与理论研究[D].南昌:南昌大学，2007.
［3］张颂阳.半固态镁合金铸轧成形技术[M].北京:冶金出版社，2008.
［4］吕书林,吴树森，戴维，等. 超声振动制备5052合金半固态浆料的研究[J].特种铸造及有色合金, 2010,（4）: 326-330.
［5］李文杰.功率超声制备铝合金半固态浆料机理初探[D].南昌:南昌航空大学，2007.
［6］卢雅琳，李森泉.铝合金半固态变形时的微观组织特征[J].塑性工程学报, 2009，（2）: 184-192.
［7］陈晓阳，毛卫民，钟雪友.半固态合金浆料挤压变形的液相偏析模型[J].北京科技大学学报，1998,20（4）:340-344.
［8］Ohno A. The Solidification of Metals[M].Tokyo:Chijin Shokan Co.,Ltd.,1976.
［9］管仁国,李建平,陈礼清,等. 波浪型倾斜板振动过程中合金组织的形成机理[J]. 材料研究学报,2008,22(4):363-368.
［10］周尧和，胡壮麟，介万奇.凝固技术[M].北京:机械出版社，1998.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】