小孔冲裁用细长凸模保护套新型制造方法

英文标题：New manufacturing method of projecting jacket used for slim punch of small holes blanking

作者：黄珍媛罗建东刘慧平

分类号：TG316

出版年,卷(期):页码：2012,37(5):109-111

摘要：

针对目前常用的小孔冲裁用细长凸模保护套制造方法存在的加工难、成本高、耐磨性不足等问题，研究了一种新型的细长凸模保护套制造方法。首先采用普通钢加工出保护套，然后通过纳米化学复合镀工艺提高保护套表面硬度和耐磨性。结果显示，通过该方法获得的镀层硬度和耐磨性与常用硬质合金高强度材料的性能相当；镀层表面能谱分析和形貌分析表明，纳米SiC粒子对增强镀层表面硬度和耐磨性具有重要作用；该方法工艺简单、成本较低，值得在工程实际中推广采用。

According to the difficulties of the common manufacturing method of the projecting jacket applied to prevent the slender punch used for small holes blanking, such as processing hard, the high cost, the wear resistance insufficient, and etc., a new manufacturing method for projecting jacket of slender punch was studied. Firstly，the projecting jacket for slender punch was processed using common steel. Then the nano chemical composite plating process was applied to improve the hardness and wear resistance of the surface of the projecting jacket. The results show that the hardness and wear resistance of the coating are as same as those of the high strength material. The surface energy spectrum and morphology analysis of the coating show that nano-SiC particles contribute to the improvement of the hardness and wear resistance of the coating surface. It is feasible to apply this new method in the practical projects.

基金项目：

参考文献：

［1］李光华.多工位级进冲压模具高速冲压时存在的问题及其对策[J].模具工业，2000，(5)：20-22.
［2］黄珍媛，阮锋，张寒，等.IT制件精密级进冲压模具关键技术的现状与发展[J].锻压技术，2005，30（5）：98-100.
［3］黄珍媛，阮锋，罗建东，等. 精密细长凸模的导向保护装置及其导向型面的强化方法:中国,ZL 2007 1 0028240.2[P].200903.
［4］黄珍媛，阮锋，罗建东，等.精密细长凸模的导向保护装置:中国,ZL 2007 2 0051963.X[P].200804.
［5］顾立民，马朋飞.高速冲模材料选用与实践[J].防爆电机，2005，（5）：34-35.
［6］孙宝琦，何平.模具用硬质合金及其进展[J].模具工业，1996，（12）：3-7.
［7］何流，何云，万长根，等.高精度多工位空调翅片硬质合金级进冲压模具的设计[J].硬质合金，1997，（11）：229-233.
［8］孙希泰.材料表面强化技术[M].北京：化学工业出版社，2005.
［9］黄珍媛,阮锋,周驰，等. 高速精密级进模表面加工工艺的开发与应用[J].模具制造,2008,(12):74-78.
［10］刘慧平. Ni\|P\|SiC（纳米）化学复合镀在拉深模表面强化中的应用研究[D].广州：华南理工大学，2007.

服务与反馈：

【文章下载】【加入收藏】