Ti-1023钛合金连接件锻件折叠缺陷分析

英文标题：Analysis of Ti-1023 titanium alloy joint forging fold

作者：齐立春黄利军刘德林刘昌奎黄旭

单位：北京航空材料研究院

关键词：Ti-1023钛合金锻件锻造折叠缩孔

分类号：TG316;TG146.4

出版年,卷(期):页码：2012,37(6):4-7

摘要：

对比分析了Ti-1023钛合金锻件折叠缺陷和铸锭内部缩孔经改锻后的缺陷差异。研究发现:Ti-1023钛合金折叠线性缺陷无明显宽窄变化、两端较圆钝，与表面呈一定角度嵌入基体，缺陷表面的氧元素含量较高，形成大量的氧化物颗粒；Ti-1023钛合金铸锭内部缩孔经改锻后的线状缺陷有明显的二次裂纹，且两端为明显的尖端，缺陷表面为自由表面特征，不含氧元素。

The differences of Ti-1023 titanium alloy forging fold defect and shrinkage holes defect by forging were studied. The results show that the width change of Ti-1023 titanium alloy forging fold defect is not obvious, both ends are round, and defect embeds in matrixes with an angle. Furthermore, the content of surface oxygen element is higher and it generates a great deal of oxide particles. However Ti-1023 titanium alloy shrinkage holes defect by forging possesses obvious second cracks, both ends are pointed. Defect surface is free surface withont oxygen element.

基金项目：

参考文献：

［1］莱茵斯 C, 皮特尔斯 M. 钛与钛合金 [M].陈振华，等译. 北京:化学工业出版社, 2005.
［2］黄伯云, 李成功, 石力开,等. 中国材料工程大典:第4卷有色金属材料工程(上) [M]. 北京:化学工业出版社, 2006.
［3］张卫方，刘庆瑔，陶春虎，等.钛合金损伤与预防的研究进展[J].材料工程，2003，（增刊）：21-24.
［4］张英明，周廉，孙军，等.钛合金冷床炉熔炼技术进展[J].钛工业进展，2007，24（4）：27-30.
［5］李梁,刘希林.钛合金膜板类锻件热模锻造成形技术研究[J].锻压技术,2010,35(6):11-13.
［6］李权,傅国如,徐志刚.锻造折叠导致发动机压缩器叶片断裂失效[J].理化检验：物理分册,2005（增刊）:392-394.
［7］陶春虎，刘庆瑔，曹春晓，等.航空用钛合金的失效及其预防[M].北京：国防工业出版社,2002.
［8］张万金，屈丽杰，刘维洲.铝合金模锻件折叠缺陷产生的原因与预防措施[J].轻金属，2002（11）：58-60.
［9］陈鑫.钛及钛合金真空自耗熔炼补缩工艺研究[J].特钢技术，2009，15（60）：39-41.
［10］段丽艳.钛铸件的缺陷及消除方法的探讨[J].轻金属,2007,(2):45-47.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】