精密冷锻模具型腔切削工艺优化的试验研究

英文标题：Investigation of cutting process optimization for cold working precision forging die

作者：马春宇袁军平吴海超

单位：广州番禺职业技术学院

分类号：TG144

出版年,卷(期):页码：2012,37(6):69-71

摘要：

以DC53模具钢为研究对象，首先通过硬度测试、冲击试验优选其最佳热处理工艺，之后以精雕机为平台进行切削试验，对比研究了进给速度与吃刀深度、路径间距不同工艺组合切削时断刀的频率。研究结果表明，DC53经过预调质处理后淬火再400 ℃回火20 min的热处理工艺最适合精密冷锻模具强韧性配比的要求，其理想的切削工艺为路径间距0.01 mm、吃刀深度0.01 mm、进给速度1.8 m·min-1，该工艺在保证一定加工效率的基础上有效避免了频繁断刀的发生。

Taking DC53 as a research object，the best heat treatment methods were selected based on hardness test and impact test, then the influences of different combinations of cutting depth, path space and feed peed on cuttingtool broken tendency were investigated by cutting test based on carver PMSRT . The results show that quenched and tempered DC53 at 400 ℃ for 20 min is suitable for cold working precision forging die, the best cutting process is 0.01 mm path space, 0.01 mm cutting depth and feed speed at 1.8 m·min-1，which avoids frequent cuttingtool broken based on a certain processing efficiency.

基金项目：

广州市教育系统首批建设创新学术团队资助项目（穗教科2009-11）

参考文献：

［1］徐耀坤.模具材料及热处理技术对模具寿命影响的研究[J].锻压技术,2002, 27 (4):62-64.
［2］曹光明.提高 Cr12MoV 钢模具寿命的热处理工艺[J]. 热加工工艺,2004, (10):4648.
［3］Lee Y C,Chen F K.Fatigue life of coldforging dies with various values of hardness[J].Journal of Materials Processing Technology,2001, 113 (13):539-543.
［4］张文玉.模具型腔的几种精整加工方法的对比分析[J].锻压技术,2005, 30 (4):42-45.
［5］辛选荣,刘汀.缓冲齿轮精密冷锻工艺及模具[J].锻压技术,2003, 28 (1):14-15.
［6］文理,陆绍勤.对锻造模具型腔制作工艺的比较研究[J].锻压技术,1998, 23 (2): 60-62.
［7］王秀文,王耀祖,蔡卫东.冷锻件工艺分析的浅析[J].锻压装备与制造技术,2003, 38 (2):34-36.
［8］韩木林.高速切削技术在连杆锻模制造中的研究和应用[J].锻压技术,2010, 35 (3):6-10.
［9］贾慈力,沈耀仁,陆文华, 等.DC53 回火特性研究[J].上海工程技术大学学报,2008, 22 (4): 336-338.
［10］黄珍媛,郭雷,阮锋.听筒 T 铁级进模冷锻工艺研究[J].锻压技术,2009, 34 (5):80-84.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】