AZ80镁合金罩盖温挤压成形工艺及模具设计

英文标题：Warm extrusion process and die design for AZ80 magnesium alloy shroud

作者：王麟平王明哲张小研张治民

关键词：镁合金罩盖温挤压模具设计

分类号：TG379

出版年,卷(期):页码：2012,37(6):87-90

摘要：

介绍了AZ80镁合金罩盖的结构特点及温挤压成形工艺和模具的设计要点。通过自行设计的温挤压模具，制备了AZ80镁合金罩盖，并对温挤压工艺方案进行了优化。结果表明：采用该工艺及模具能生产出表面质量较好，形状完整的罩盖；在挤压温度为280～400 ℃之间，挤压速度为10 mm·s-1，模具预热温度为150~300 ℃时，镁合金罩盖的成形性能最好。

The structural features of AZ80 magnesium alloy shroud and keys about warm extrusion process and die design were described. The type of AZ80 magnesium alloy shroud was prepared and the extrusion process parameters were optimized by selfdesigned warm extrusion die. The results show that the shroud is prepared with excellent surface quality and fine dimensional accuracy. The best forming property of the magnesium alloy shroud is got under the conditions that the extrusion temperature is between the 280400 ℃, extrusion rate is 10 mm·s-1 and preheat temperature of the die is between 150300 ℃.

基金项目：

参考文献：

［1］姚素娟,张英.镁及镁合金的应用与研究[J].世界有色金属,2005,7(1):26-30.
［2］王强,张治民，张宝红，等.镁合金变形强韧化研究进展[J].材料导报,2006，20（6）： 431-433.
［3］王志虎, 张菊梅，袁森,等. 镁合金强韧化处理研究进展[J]. 铸造技术,2006,27(1):84-86.
［4］史庆志,刘永长,李宝银.镁基合金强韧化的新思路[J].材料导报， 2004，18（11）:26-29.
［5］陈刚. 镁合金负重轮温挤压成形工艺研究[D].太原：中北大学，2009.
［6］周永泰.我国汽车冲压模具的现状与发展[J].汽车与配件，2007，29（14）：6-12.
［7］杨长顺.冷挤压模具设计[M].北京：国防工业出版社,1994.
［8］王达健，谢刚，戴永年.低密度汽车镁材料[J].中国有色金属学报,1997,7(1)：390-393.
［9］杜文博.镁合金在交通工具中的应用现状[J]. 世界有色金属，2006，2(6)：19-21.
［10］师昌绪，柯俊Caln R W. 材料科学与技术丛书：第8卷[M].北京：科学出版社，1999.
［11］奇克敏，丁桴.材科成形工艺学[M].北京：冶金工业出版杜，2006.
［12］段亚利. AZ31镁合金薄壁管材挤压成形工艺研究[D].太原：中北大学，2006.
［13］壬忠堂，张士宏，莫立华,等.镁合金管材挤压工艺与组织性能研究[J].锻压机械，2002,11(1): 60-63.
［14］王渠东，吕宜振，曾小勤,等. 镁合金在电子器材壳体中的应用[J].材料导报，2004，14（6）：22-24.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】