中碳合金钢零件成形技术研究
英文标题:Research on forming technology of medium carbon alloy steel parts
作者:韩来福 尹小平 马涛 范酉根  赵红勋 
单位:内蒙古第一机械集团有限公司 
关键词:中碳合金钢 数模 回弹 裂纹 
分类号:TG386
出版年,卷(期):页码:2013,38(1):172-174
摘要:

针对中碳合金钢零件在成形时产生的裂纹、裂口与回弹问题,通过增加退火工艺,明显改善了零件的成形性能,消除了零件的成形裂纹,使伸长率从12%提高到了25%。从零件的符合性考虑,通过对零件的受力状态进行分析,确定了零件的回弹量,将零件在R25 mm位置处产生回弹的圆弧弦高值由原来的1.7 mm改进为2.7 mm,通过计算将R25 mm修改为R16.5 mm,取得了很好的实验效果。采用计算机软件AUTO  FROM建立数模,并按数模加工模具工作型面,更好的保证了模具工作部分形状与模具图纸的符合性。

To address the issues of cracks and the spring back of the medium carbon alloy steel parts, the annealing process was added to improve the formability of the parts. The forming cracks were eliminated, and the elongation was increased from 12% to 25%.The spring back amount was confirmed by analysis of the parts conformity and stress condition. After calculation, the spring back spot R25 mm was changed into R16.5 mm and the circular chord height was changed from 1.7 mm to 2.7 mm. The die surface was processed according to the digital analog set up by AUTO FROM to guarantee that the shape of the die working part is conformed to the drawings.
 

基金项目:
作者简介:
参考文献:


[1]汪祥支,苏超,周锐,等.汽车保险杠拉深成形数值分析与工艺优化[J]. 锻压技术,2008,33(1): 45-59.
[2]邓陟,王先进,陈鹤峥. 金属薄板成形技术[M]. 北京:兵器工业出版社,1993.
[3]陈刚,李科峰,杜之明,等. 特种车辆履带板热压成形技术研究 [J] . 锻压技术,2010,35(6): 27-30.
[4]刁可山,蒋浩明,曹猛,等.基于CAE的DP600高强钢零件回弹特征分析及控制[J]. 锻压技术,2010,35(5): 47-51.
[5]宋黎,杨坚,黄天泽. 板料弯曲成形的回弹分析与工程控制综述[J]. 锻压技术,1996,21(1): 18-22.
[6]史美堂. 金属材料与热处理[M]. 上海:科学技术出版社,1980.
[7]汪大年. 金属塑性成形原理[M]. 西安:机械工业出版社,1982.
[8]虞松,冯维明,王戌. 金属韧性断裂准则的实验研究[J]. 锻压技术,2010,35(1): 121-124.
[9]杨锋平,孙秦.韧性金属渐进断裂的有限元法研究[J]. 金属学报,2008,44(4): 489-494.
[10]王孝培.  冲压设计资料[M].北京:机械工业出版社,1983.

 

服务与反馈:
文章下载】【加入收藏
《锻压技术》编辑部版权所有

中国机械工业联合会主管  中国机械总院集团北京机电研究所有限公司 中国机械工程学会主办
联系地址:北京市海淀区学清路18号 邮编:100083
电话:+86-010-82415085 传真:+86-010-62920652
E-mail: fst@263.net(稿件) dyjsjournal@163.com(广告)
京ICP备07007000号-9