锻压技术

基于拉伸试验的板料成形性能研究

英文标题：Study of sheet metal forming performance based on tensile test

作者：丁华薛松张东张维

单位：西南科技大学

关键词：板料成形 DC06钢材料取向拉伸速率

分类号：TG335

出版年,卷(期):页码：2013,38(2):37-39

摘要：

板料的成形性能不仅取决于板料本身的材料特性也取决于板料的各向异性以及成形工艺条件，比如成形速度。以DC06冷连轧低碳钢板为研究对象，探讨了板料在不同取向和不同变形速度下的力学性能，并应用WDW-100微机控制电子万能试验机,对不同取向的DC06钢板料试件在不同拉伸速率下进行试验。试验分析结果表明： DC06对拉伸速度敏感，当拉伸速率为10mm·min-1时材料成形性能最好；材料取向对于成形性有一定的影响。

Sheet metal forming performance depends not only on the materials properties of sheet metal itself and the sheet metal anisotropic and forming process conditions, such as forming speed. Taking DC06 steel as an research object,the mechanical properties of sheet material of different orientations and different deformation speeds were studied. The DC06 steel material specimen of different orientation was studied by WDW-100 microcomputer control electronic universal testing machine, using different tensile rate. The results show that DC06 is sensitive to tensile rate and when the tensile rate is 10mm·min-1, the forming properties of the material are best, and the material orientation has a relatively large impact on its formability.

基金项目：

西南科技大学大学生创新基金资助项目（CX11-073)

参考文献：

［1］林启中，林长华. 拉伸速度及试样对力学性能的影响[J]. 物理测试，1989，（7）：3-5.
［2］薛松, 周杰, 何应强. 差厚拼焊板成形性的单向拉伸试验[J]. 锻压技术，2011，36（2）：30-33.
［3］GB／T 2282002，金属拉伸试验方法[S].
［4］倪洪启，刘相华，王国栋. 超级钢板料冲压性能的拉伸试验研究[J]. 材料科学与工艺,2008，16（5）：702.
［5］丁富连，汪承璞，陈卓人. 冷轧薄钢板基本成形性能指标影响因素分析[J]. 宝钢技术，2000,（5）：40-44.
［6］吴向东，万敏，周贤宾. 各向异性板料屈服轨迹的研究[J]. 材料科学与工艺，2004，12（4）：391-397.
［7］Sebastian Dziallach，Wolfgang Bleck，Michael Blumbach,et al. Sheet metal testing and flow curve determination under multiaxial conditions[J]. Advanced Engineering Materials，2007，9(11)：987-994.
［8］Durmus A. The effect of strain rate on mechanical properties of cold forming sheet metals[J]. Material Wissenschaft and Werkstofftechnik，2009，40(9)：699-703.
［9］刘文静. 材料的机械性能对板料的成形性能的影响[J]. 科学时代，2009，（1）：84-86.
［10］王艳侠. 金属室温拉伸中拉伸速度对试验结果的影响[J]. 机械管理与开发，2010，25（5）：95-96.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】