锻压技术

大口径Φ219mm×4.5mm BFe10-1-1白铜管生产工艺研究

英文标题：Study on production process of large diameter Φ219mm×4.5mm BFe10-1-1 cupronickel tube

作者：陈琴刘广龙张娟柏先林

单位：金川集团

分类号：TG146

出版年,卷(期):页码：2013,38(2):69-73

摘要：

针对本企业拥有的大吨位熔炼与铸造机组、挤压机和拉拔机等设备，开发高附加值的舰船用大口径白铜管。通过对铸造、挤压、拉伸及退火等工序的产品进行生产现场跟踪，对工艺参数进行优化，对最终产品进行化学成分、金相组织、氧氮含量、力学性能及断口试验等性能的分析研究。经过对工艺参数的优化调整，最终成功开发生产出Φ219mm×4.5mm BFe10-1-1大口径白铜管，产品性能满足国标及客户要求，并已实现批量化生产。

Large diameter cupronickel tube with high valueadded for ship was developed using largetonnage smelting and casting units,press machine and drawing machine and soon. By tracking the casting, extrusion and stretching and annealing processes of products on site, the process parameters were optimized. The final product chemical composition, microstructure, oxygen nitrogen content, mechanical property and fracture test were analyzed and studied. Through the optimization of process parameter adjustment, Φ219mm×4.5mm BFe10-1-1 large diameter cupronickel tube with the performance met the national standards and customers requirements was successfully developed, and the mass production was achieved finally.

基金项目：

参考文献：

［1］钟卫佳. 铜加工实用技术[M].北京：冶金工业出版社，2007.
［2］曾宪金. BFe 10-1-1l白铜管生产工艺[J].甘肃有色冶金,1994,(1):33.
［3］狄大江.舰船用铜及铜合金管[J].有色金属加工,2011，40(1):32.
［4］GB/T 5231—2001,加工铜及铜合金化学成分和产品形状[S].
［5］GB/T 228—2002,金属材料室温拉伸试验方法[S].
［6］GB/T 13298—1991,金属显微组织检验方法[S].
［7］付亚波.铜合金冷凝管及其新加工技术[J].有色金属加工,2005,34（2）：40.
［8］黄璐琼，武兴伟.铜镍合金管在舰船海水管系中的应用[J].船舶，2011，(1)：40.
［9］邓楚平，黄伯云，潘志勇. 退火工艺对冷凝器用白铜管组织和性能的影响[J].金属热处理，2006,(11):58.
［10］GB/T 1527—2006，铜及铜合金拉制管[S].
［11］YS/T 662—2007，铜及铜合金拉制管[S].

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】