轴类零件冷锻成形的预成形工步设计及优化

英文标题：Preform step design and optimization of cold forming for axial parts

作者：霍中雪高锦张贾俐俐

单位：1.东南大学材料科学与工程学院江苏省先进金属材料高技术研究重点实验室江苏南京211189 2.南京交通职业技术学院江苏南京 211188

分类号：TG316

出版年,卷(期):页码：2012,37(4):22-29

摘要：

以大高径比轴对称锻件的预成形设计为例，以预锻工步多目标的优化设计为目的，提出一种预成形新方法。从给定的最终成形件形状出发，基于Deform-3D软件进行数值模拟，采用正向设计，初步计算各预成形工步的几何参数，充分考虑了模腔的充填、降低终锻力、提高变形均匀性及减小材料最大损伤值等方面因素后，从终锻工步出发，逆向调试并优化各预成形工步的参数，并将模拟结果与实验结果作比较。实验结果表明，逆向技术在多工步锻造的预成形工步设计上具有指导意义。

Taking preform design of an axisymmetric forging with large ratio of height to diameter as an example, aiming to achieve multiple-target optimization design for pre-forging steps, a new preform method was put forward. Proceeding from the shape of final forging, numerical simulation was based on Deform-3D.By forward design, geometric parameter of each pre-forging step was preliminarily calculated. Taking full consideration of cavity filling, decrease of final forging force, increase of deformation uniformity and reduction of maximum material damage, the parameters of each preform step were debugged conversely and optimized from final forging step. A comparison was made between the simulation result and the experiment result. The experimental results show that the reverse technology is instructional to preform step design of multi-step forming.

基金项目：

参考文献：

［1］赵国群，阮雪榆，关廷栋.预成形设计的新方法——反向模拟技术[J].模具技术，1991，(3)：1-6.
［2］胡亚民，华林.锻造工艺过程及模具设计[M].北京：北京大学出版社，2006.
［3］姚泽坤.锻造工艺学与模具设计[M].陕西：西北工业大学出版社，2007.
［4］王以华.锻模设计技术及实例[M].北京：机械工业出版社，2009.
［5］罗仁平，彭颖红，张永清.锻造过程的优化目标建模[J].机械科学与技术，1999，18(6)：963-965.
［6］高锦张，贾俐俐，陈文琳.塑性成形工艺与模具设[M].北京：机械工业出版社，2001.
［7］杨雨春，夏巨谌，胡国安.镦粗长轴类锻件避免失稳研究[J].锻压技术,1999，21(2)：6-8.
［8］郑勇，高锦张，贾俐俐. 基于有限元模拟的锥模局部镦粗工艺研究[J].锻压技术，2006，31(4)：96-99.
［9］Sabih A，Nemes J A. Internal ductile failure mechanisms in steel cold heading process[J].Journal of Materials Processing Technology，2009，209(9)：4292-4311.
［10］牟华，高锦张，贾俐俐.冷锻过程局部镦粗规则的研究及应用[J].锻压技术，2006，31(2)：78-81.

服务与反馈：

【文章下载】【加入收藏】