2A12合金的无润滑管材挤压工艺实验研究

英文标题：Research of 2A12 alloy pipe extrusion process experiment with no lubrication

单位：兰州理工大学

分类号：TG376.9

出版年,卷(期):页码：2012,37(4):51-54

摘要：

为了在国产35 MN挤压机上实现2A12合金管材的无润滑挤压，减少废品的产生，通过分析2A12合金的材料性能及国产35 MN挤压机的结构特点，对挤压机的穿孔针系统结构进行改造，并在该挤压机上进行了2A12合金的无润滑管材挤压实验。实验结果表明，在合理控制挤压速度、挤压温度、铸锭加热温度等工艺参数的条件下，可以实现2A12合金的无润滑管材挤压；挤压产品的内表面质量好，偏心度得到很大改善。

In order to complete no lubrication extrusion on domestic 35 MN extruder, and reduce waste generation, by analyzing the material properties of 2A12 alloy and the structure characteristics of domestic 35 MN extruder, the transform of the extruder perforation needle system structure was performed and a no lubrication pipe extrusion experiment of the 2A12 alloy pipe on the machine was made. The experimental results show that the no lubrication pipe extrusion of 2A12 alloy can be realized in the proper control of process parameters, such as the extrusion speed,extrusion temperature and heating temperature.The inner surfaces of the extrusion product has good quality, its eccentricity is also improved greatly.

基金项目：

参考文献：

［1］赵世庆.对我国铝加工产业发展战略的浅见与建议[J].铝加工，2006，（3）：1-6.
［2］海朝智.2A12铝合金板材包铝层横向分布不均原因及对策[J].轻合金加工技术，1999，27（6）：16-19.
［3］邓小民.无润滑挤压铝合金管材时铸锭长度的确定[J].重型机械，2001，（4）：39-40.
［4］曾苏民，袁季岗.我国迎来加快迈向世界铝加工强国的发展机遇[J].功能材料，2010，7（2）：7-10.
［5］刘静安.铝型材挤压模具设计、制造、使用及维修[M].北京：冶金工业出版社，2002.
［6］赵云路，刘静安.铝型材工模具设计与生产工艺优化[M].重庆：西南铝信息中心出版，1998.
［7］邓小民. 无润滑挤压铝合金管工艺参数的确定[J].轻合金加工技术，2002，30（4）：25-26.
［8］肖亚庆，谢水生，刘静安，等.铝加工技术实用手册[M].北京：冶金工业出版社，2005.
［9］宋禹田，赵海滨，铝合金挤压管材内擦伤的分析[J]. 轻合金加工技术，2005，33（1）：38-41.
［10］王丽巍，闫德民. 解决35 MN水压机管材偏心的措施[J]. 轻合金加工技术，2002，30（11）：33-35.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】