成形加强筋工艺研究与模具设计

英文标题：Forming process study and mold design of stiffener

关键词：反顶成形加强筋起皱翘曲刚度

分类号：TG386

出版年,卷(期):页码：2013,38(3):118-121

摘要：

针对成形加强筋时产生起皱、翘曲、缩颈、裂纹的缺陷，进行成形加强筋的工艺分析计算，并在实际生产中进行试冲调试，经过批量生产后，总结了不同厚度、不同材料成形加强筋的最佳工艺参数。成形加强筋后，在零件不产生缩颈、裂纹的前提下，加强筋的高度h达到最大值，解决了提高零件刚度与产生裂纹的矛盾。利用成形设备油压机气垫力能够滞后于主缸压力的功能，改进模具结构，在模具结构上采用设备主缸压力压料、气垫反顶成形加强筋的新思路，解决了零件起皱、翘曲的缺陷，大大减少了校平的工作量，取得了较好的效果。

To deal with the wrinkling, wrapping, necking and cracking during the stiffener forming process, the stiffener forming technology was analyzed and calculated. After the trial stamping, adjustment in real situation and the mass production, the optimum technology parameters of the stiffener of various thicknesses and materials were summarized. With the parameters, the height of the stiffener reaches the maximum without having necking and cracking, which solves the contradiction between stiffness improvement and crack. The die structure was improved according to the feature that the cushion power of the oil hydraulic press lagging behind the pressure of the main cylinder. A new idea was applied: the main cylinder was used for swaging, and the air cushion was used for back punching to form the stiffener. In this way, the wrinkling and wrapping problems are solved and the workload during roll smoothing is reduced, which achieves good effect.

基金项目：

参考文献：

［1］肖士昌，高锦张，贾俐俐，等. 单道次渐进成形锥型件壁厚均匀临界成形角的研究[J].  锻压技术，2012，37（1）:49-54.Xiao S C,Gao J Z,Jia L L. et al. Research on critical forming angle of uniform thickness in single\|path incremental forming for conical part[J].Forging  & Stamping Technology, 2012，37（1）:49-54.
［2］虞松，冯维明，王戎.金属韧性断裂准则实验研究[J]. 锻压技术，2010,35（1）: 121-124.Yu S ,Feng W M,Wang R.Research on ductile fracture criterion in plastic deformation processes[J].Forging  & Stamping Technology, 2010,35（1）: 121-124.
［3］王孝培.  冲压设计资料[M] . 北京：机械工业出版社，1983.Wang X P. Stamping Design Material [M]. Beijing: China Machine Press, 1983.
［4］邓陟，王先进，陈鹤峥 . 金属薄板成形技术[M]. 北京：兵器工业出版社，1993.Deng Z,Wang X J,Chen H Z. Forming Technology of Metal Sheet [M].  Beijing: Weapon Industry Press, 1993.
［5］刁秋梅，姜允程. 篷布护铁冲压工艺与模具设计[J]. 锻压技术，2010,35（4）: 99-101.Diao Q M,Jiang Y C.Design of stamping process and die structure for tarpaulin guard iron [J].  Forging  & Stamping Technology, 2010,35（4）: 99-101.
［6］杨锋平，孙秦.韧性金属渐进断裂的有限元法研究[J] . 金属学报，2008,44（4）: 489-494.Yang F P，Sun Q. Algorithm study of gradual fracture of ductile metallic material with finite element method [J]. Acta Metallurgica Sinica, 2008,44（4）: 489-494.
［7］李伟峰，乔明杰.杯突试验测定板料成形极限图的试验研究[J] . 锻压技术，2010,35（6）: 63-65.Li W F,Qiao M J. Experimental study on determinating forming limit diagram of shcct mctal with cupping test method [J].   Forging  & Stamping Technology, 2010,35（6）: 63-65.
［8］袁迎建，韩来福. 防止铝合金油箱零件冲裂[J] . 新技术新工艺，2012,（1）: 84-87.Yuan Y J,Han L F. Prevention of avulsion of aluminumalloy gasoline tank parts [J]. New Technology & New Process, 2012,（1）: 84-87.
［9］王玥，傅建，朱梅云,等. 125摩托车油底壳拉深起皱现象分析与解决[J]. 锻压技术，2010,35（2）: 127-131.Wang Y,Fu J,Zhu M Y, et al. Drawing wrinkling analysis and solution of 125 motorcycle tank bottom shell [J].Forging  & Stamping Technology, 2010,35（2）: 127-131.
［10］王书恒，王元勋，陈建桥,等.矩形盒拉深时摩擦润滑条件与压边力的有限元分析[J].模具技术,2006,（2）：48-51.Wang S H,Wang Y X, Chen J Q. et al.  The FEM analysis of friction lubrication condition and pressurepad\|force of drawing of rectangular box. [J]. Die and Mould Technology,2006,（2）：48-51.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】