4Cr16Mo石化主轴锻造工艺研究

英文标题：Research on forging process of 4Cr16Mo petrochemical axle

作者：叶玉娟高全德孙振环张伟

单位：中原特钢股份有限公司

关键词：4Cr16Mo 主轴锻造工艺裂纹

分类号：TG335.55

出版年,卷(期):页码：2013,38(5):33-37

摘要：

石油化工主轴的受力情况比较复杂，需要承受较大冲击和交变载荷的作用，要求具有良好的综合力学性能。4Cr16Mo材料具有较高硬度、耐磨性及耐冲击性，能够满足使用中的性能要求；但塑性较差，变形抗力大，锻造温度范围较窄，锻造工艺存在较大难度。本文通过生产跟踪，对生产工艺进行优化：确定锻造温度范围为800～1150 ℃，低温段缓慢加热；锻造时采用上平、下V砧，严格控制压下量，高温时采用分散小变形，并严格执行锻后退火及性能热处理，大大减少了主轴开裂，在生产中取得了良好的效果。

Petrochemical axle works under complex stresses of bigger impulsive force and alternate loading，which is needed to have a good integrated mechanical performance. 4Cr16Mo possesses high hardness, wear and resistance of impulsive force，which can meet the requirements of petrochemical axle. But，for the poor plasticity, high resistance of transmutation and narrow range of forging temperature, it is hard to be forged. Through summing up and analyzing the puzzles in practice, the forging process was optimized: the forging temperature was 800-1150 ℃，with slowly heating during the low temperature. The upper flat and lower V anvils were adopted, and the transmutation was controlled accurately. Small transmutation was commanded in high temperature, and rigidly controlled the annealing after forging and heat treatment. Finally，the axle cracking was gradually reduced and the good quality was received in the productive practice.

基金项目：

叶玉娟（1983-），女，硕士，助理工程师

参考文献：

［1］赵嘉蓉,赵刚.金属塑性加工的冶金学基础[M].北京:冶金工业出版社,1995.Zhao J R,Zhao G.Metal Base of Metallurgy on Metal Plastic Processing[M].Beijing:Metallurgical industry Press,1995.
［2］崔忠圻.金属学与热处理[M].北京：机械工业出版社,2000.Cui Z Q.Metallography and Heat Treatment[M].Beijing:Mechanical Industry Press,2000.
［3］俞汉清,陈金德.金属塑性成形原理[M].北京:机械工业出版社,1998.Yu H Q,Chen J D.Principle of Metal Plastic Forming[M].Beijing: Mechanical Industry Press,1998.
［4］姚泽坤.锻造工艺学与模具设计[M].西安:西北工业大学出版社,1996.Yao Z K.Forging Technology and Die Design[M].Xian:Northwestern Polytechnical University Press，1996.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】