锻造工艺对钢中组织偏析的改善

英文标题：Segregation improvement in steel by changing forging technology

作者：向小琴喻涛

关键词：组织偏析锻造扩散退火加热温度

分类号：

出版年,卷(期):页码：2014,39(1):11-14

摘要：

针对某些大中型合金钢锻件金相组织中经常出现不同程度偏析的质量问题，研究了解决该问题的措施。以某船用柴油机连杆42CrMo和某输入齿轮轴17CrNiMo6为研究对象，通过提高锻造的加热温度（连杆为1250 ℃，输入齿轮轴为1280 ℃）、增加镦拔次数（由直接拔长成形改为三镦三拔后成形）、在加热温度下保温足够时间（连杆为2 h，输入齿轮轴为2.5 h）的工艺方案，有效地改善了锻件的微观组织偏析。

To solve the quality problem of different degree tissue segregation in large or middle-size alloy steel forgings,the corresponding measures were studied. Taking 42CrMo diesel engine link rod and 17CrNiMo6 input gear roller as research objects,the forging micro-tissue segregation was improved effectively by improving forging temperature(link rod is 1250 ℃ and input gear roller is 1280 ℃), increasing upsetting times(upsetting and stretching for three times instead of directly stretching) and keeping warm for enough time at forging temperature(link rod is 2 h and input gear roller is 2.5 h).

基金项目：

向小琴（1976-），女，学士，工程师

参考文献：

[1]杨小垒，邓德伟，陈伟，等.25Cr2Ni3Mo叶轮开裂失效分析[J].锻压技术，2011，36（6）：4-6.

Yang Xiaolei, Deng Dewei, Chen Wei, et al. Crack failure analysis of 25Cr2Ni3Mo impeller [J]. Forging & Stamping Technology, 2011,36(6)：4-6.

[2]霍中雪，高锦张，贾俐俐.轴类零件冷镦成形的预成形工步设计及优化[J].锻压技术，2012，37（4）：22-29.

Huo Zhongxue, Gao Jinzhang, Jia Lili. Preform step design and optimization of cold forming for axial parts [J]. Forging & Stamping Technology, 2012, 37(4)：22-29.

[3]蔡珣.材料科学与工程基础[M].上海：上海交通大学出版社,2010.

Cai Xun. Materials Science and Engineering Foundation [M].Shanghai： Shanghai Transport University Press, 2010.

[4]中国机械工程学会锻压学会.锻压手册[M]. 3版.北京:机械工业出版社，2002.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】