淬火与回火温度对热作模具钢组织与性能的影响

英文标题：Effect of quenching and tempering temperature on microstructure andperformance of hot-work die steel

作者：李海东

单位：连云港职业技术学院

分类号：TG316

出版年,卷(期):页码：2014,39(9):111-115

摘要：

对热作模具钢进行了淬火与回火热处理，研究了淬火温度与回火温度对模具钢硬度与抗热疲劳性能的影响，观察了模具钢的冲击断口形貌和热循环疲劳断口特征，优化了热作模具钢的淬回火工艺，并分析了其对热疲劳性能的影响规律和作用机理。结果表明，1080 ℃淬火后的模具钢的疲劳裂纹的主裂纹最短，且裂纹较为细小，经过此温度淬火后的试样具有较好的热疲劳抗力；580 ℃+560 ℃回火后的试样表现出了良好的热疲劳抗力性能。

After quenching and tempering for the hot-work die steel, the effect of quenching temperature and tempering temperature on the hardness and thermal fatigue resistance of die steel was studied, the broke mouth shape of the impact fracture and broke mouth characteristic of the thermal cycling fatigue fracture of die steel were observed, the quenching and tempering technology of hot-work die steel was optimized and its influence regulation and mechanism of action on heat fatigue properties were also analyzed. The results show that the main crack of fatigue crack is the shortest and the smallest at 1080 ℃, so the samples after quenching at 1080 ℃ have a better thermal fatigue resistance; 580 ℃ +560 ℃ tempering samples show good performance of thermal fatigue resistance.

基金项目：

江苏省连云港科技发展计划项目

李海东（1969-），男，硕士，副教授

参考文献：

［1］周小平, 胡心彬, 江锋. 新型热作模具钢的热疲劳性能[J]. 金属热处理, 2011,36(1): 107-109.Zhou X P, Hu X B, Jiang F . The thermal fatigue property of new hot work die steel[J]. Metal Heat Treatment, 2011,36 (1): 107-109.
［2］Murtaza G . Empirical corrosion fatigue life prediction models of a high strength steel[J]. Engineering Fracture Mechanics, 2000, (67): 461-474.
［3］徐进. 模具钢[M]. 北京：冶金工业出版社， 2002.Xu J. Die Steel[M]. Beijing:Metallurgical Industry Press,2002.
［4］Glowacki M. The mathematical modeling of thermo-mechanic processing of steel during multi-pass shape rolling[J]. Material Processing Technology,2005,(168):336-343.
［5］Matlock D K, Alogab K A, Rehards M D. Surface processing to improve the fatigue resistance of advanced bar steels for automotive applications[J]. Mater. Res., 2005,8(4):453-459.
［6］徐戊矫,丁永峰,王鹏程. 回火温度对堆焊模具耐磨性的影响[J]. 金属热处理, 2013,38(4): 85-87. Xu W J, Ding Y F, Wang P C. Effect of tempering temperature on the wear resistance of die steel[J]. Metal Heat Treatment, 2013,38 (4): 85-87.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】