小半径薄壁管内胀推弯成形模拟与实验分析

英文标题：Simulation and experiment analysis of inner bulging and push bending process for thin-wall tubes with small radius

作者：孟忠良1 卢宇鹏2 于江龙3

关键词：内胀推弯断裂弯曲半径模具结构

分类号：

出版年,卷(期):页码：2015,40(4):116-120

摘要：

通过拉弯、滚弯及数控弯曲等传统方法对Φ10 mm×1 mm、Φ20 mm×1 mm、Φ30 mm×1 mm三种规格管件进行弯曲加工实验。针对传统方法加工中出现的断裂、内侧壁厚增厚、外侧壁厚减薄、起皱和椭圆度差等问题设计了推弯模具，利用Deform软件建立了内胀推弯成形模型并进行仿真分析。在模拟过程中，对不同内压下的每一类型的管件采集数据绘制壁厚变化曲线，选取3条波动较小的曲线进行对比，最后确定模拟效果最好的内压值。依据模拟结果，通过实验对3种规格的弯管进行内胀推弯成形实验，结果表明，该方法很好地解决了小半径弯管内外壁厚度不均匀、起皱、断裂等问题。

For three kinds of specification pipes of Φ10 mm×1 mm、Φ20 mm×1 mm、Φ30 mm×1 mm, bending experiments were conducted by the traditional methods of bending, roll bending and CNC bending. In view of the fracture, inside wall thickening, outside wall thinning，wrinkling and poor ovality etc. existed in the traditional methods processing，push bending die was designed. The inner bulging and push bending model was establish and simulated by the Deform software. During the simulation, the thickness change curves were obtained through data collection for three kinds of specification pipes with different inner pressures, then three curves with small fluctuation were selected to compare. Finally, the inner pressure of the best simulation effect was determined. Based on the simulation results, experiments of inner bulging and push bending process based on three kinds of specification pipes were carried out. The results show that the problems of uneven thickness of inside and outside wall, wrinkling and fracture for bending tubes with small radius are well solved by the above method.

基金项目：

贵州省重大专项课题基金（20116017）

孟忠良（1981-），男，硕士研究生

参考文献：

[1]王新鹏. TP2铜管弯曲工艺研究[D].沈阳:沈阳理工大学,2013.

Wang X P.Rotation Bending Processing Research on the TP2 Copper Tude[D].Shenyang: Shenyang University of Technology,2013.

[2]赖欣武.基于神经网络组合预测的板料冲压回弹预测研究[D].杭州:浙江大学,2006.

Lai X W.Research on Springback Forecasting of Sheet Metal Stamping Based on a Combination Forecasting Method of Artificial Neural Network[D].Hangzhou: Zhejiang University,2006.

[3]高鹏. 6063铝合金复杂截面热管压弯装置及工艺研究[D].哈尔滨:哈尔滨工业大学,2008.

Gao P.Device and Processing of Press Bending for 6063 Aluminium Alloy Heat Tube with Complicated Section[D].Harbin: Harbin Institute of Technology,2008.

[4]李秋强.薄壁管充液压弯的数值模拟和实验研究[D].哈尔滨:哈尔滨工业大学,2009.

Li Q Q.Numerical Simulation and Experimental Research of Thin-walled Tube Press-bending with Internal Pressure[D].Harbin: Harbin Institute of Technology,2009.

[5]陈志勇,樊志新. 60 t铜排拉拔机液压缸的设计与分析[J].机械,2012, 39(8):22-24.

Chen Z Y,Fan Z X. Design and analysis of hydraulic cylinder of 60 tons copper drawing machine[J]. Machinery,2012, 39(8):22-24.

[6]古涛,鄂大辛,任颖,等. 管材弯曲壁厚变形的有限元模拟与试验分析[J]. 模具工业,2006, 32（4）:17-20.

Gu T,E D X, Ren Y,et al. Finite element simulation and experimental analysis of wall thickness deformation in the process of pipe bending[J]. Die & Mould Industry,2006, 32（4）:17-20.

[7]余胜娟. 汽车副车架单根钢管液压成形的数值模拟[D].洛阳:河南科技大学,2008.

Yu S J.Numerical Simulation of Automobile Engine Cradle with Single Steel Tube Hydro-forming[D]Luoyang: Henan University of Science and Technology,2008.

[8]窦万波.10000 m3天然气球罐用WEL-TEN610CF钢焊接工艺试验研究[J].化工机械,2007, 34(2):69-73.

Dou W B. 10000 m3 gas tank with WEL-TEN610CF steel welding technology test[J]. Chemical Machinery, 2007, 34(2):69-73.

[9]徐卫平,伍权,白文斌,等. 小半径薄壁管材内胀推弯成形制造工艺研究[J]. 锻压技术,2008,33(5):106-109.

Xu W P,Wu Q,Bai W B,et al.Study on bulging and trust bending process with small radius of thin-wall tubes[J].Forging & Stamping Technology,2008,33(5):106-109.

[10]刘劲松,张兴华,刘海,等.薄壁钢管内胀推弯成形数值模拟及实验研究[J].锻压技术,2012,37(2):63-67.

Liu J S,Zhang X H,Liu H, et al.Numerical simulation and experimental research on internal expansion push bending of thin-walled tube[J].Forging & Stamping Technology,2012,37(2):63-67.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】