2205双相不锈钢冷轧过程中磁性的研究

英文标题：Study on magnetism of 2205 duplex stainless steel during cold rolling

作者：冯志慧李静媛王一德

单位：北京科技大学

关键词：冷轧磁性铁素体测量仪

分类号：

出版年,卷(期):页码：2015,40(7):135-140

摘要：

针对2205双相不锈钢冷轧过程中磁性发生显著变化的问题，通过室温冷轧（70%压下率）的方法对冷轧前后材料的磁性用光学显微镜（OM）、铁素体测量仪、X-射线衍射和EBSD做了研究。结果表明：由于双相不锈钢常温下冷轧过程中α相不发生分解，且材料中Cr超过20%，γ相在冷轧过程中不容易发生马氏体转变，硬度测量也没有显示发生马氏体转变。铁素体仪测量冷轧后试样和原始铸态相比示数下降15%，主要来源于轧制过程中铁素体磁性的变化。冷轧过程中晶粒发生细化、铁素体在冷变形过程中位错发生缠结生成大量的亚晶界、变形导致的内应力场以及织构的影响，使铁素体的磁性发生显著的下降。

The question that why 2205 magnetic of duplex stainless steel dramatically changes during cold rolling was explained. The materials magnetism change before and after cold rolling was studied by cold rolling (up to the effective strain of 70%).The magnetism change was measured by optical microscopy (OM), ferrite meter measurement, X-ray diffraction and EBSD. The results show that, ferrite decomposition of dual phase stainless does not occur at the normal temperature during cold rolling, and there will be little stain-induced martensite transformation as Cr in material is more than 20%, and the content of hardness measurements also show no martensitic transformation. Compared with cast samples, the ferrite content value of cold rolling samples drops by 15% with ferrite meter. Among the related factors that might influence magnetism, the change of ferrite meter mainly comes from the ferrite magnetism change during cold rolling process. The influence from grain refinement, subgrain boundary generated by dislocation tangles, internal stress field caused by large deformation and texture will significantly decrease the magnetism of the ferrite.

基金项目：

国家自然科学基金资助项目(51174026)；十二五国家科技支撑计划(2012BAE04B02)

冯志慧(1988-)，女，博士研究生

参考文献：

[1]孙长庆. 双相不锈钢的发展. 性能与应用(三)[J]. 化工设备设计,1999, 36(1):41-51.

Sun C Q.The development of duplex stainless steel[J]. Performance and Application,1999,36(1):41-51.

[2]李少峰，任学平，李殊霞，等. 初始应变速率对00Cr22Ni5 Mo3N双相不锈钢超塑性的影响[J]. 锻压技术, 2013, 38 (5): 158-161.

Li S F，Ren X P，Li S X，et al. Effect of initial strain rate on superplasticity of 00Cr22Ni5Mo3N duplex stainless steel[J]. Forging & Stamping Technology, 2013, 38 (5): 158-161.

[3]李静媛，杨智辉. 超级双相不锈钢00Cr32Ni7Mo3.5N的热塑性及高温组织演变[J]. 锻压技术, 2013, 38 (6): 122-127.

Li J Y，Yang Z H. Thermo-plasticity and high-temperature microstructure evolution of hyper duplex stainless steel 00Cr32 Ni7Mo3.5N[J]. Forging & Stamping Technology, 2013, 38 (6): 122-127.

[4]刘翠珍. 双相不锈钢在中国的应用及生产[R]. 北京: 不锈钢分会专家实地调研双相不锈钢, 2002.

Liu C Z. Application of duplex stainless steel and production in China[R].Beijing: Expert of Stainless Steel Branch Investigation of Duplex Stainless Steel,2002.

[5]辛选荣, 赵文龙,谢田. TB8钛合金常温压缩应力应变曲线分析[J]. 锻压技术，2014，39（1）：126-130.

Xin X R，Zhao W L，Xie T. Analysis of TB8 titanium alloy compression stress-strain curve at room temperature[J]. Forging & Stamping Technology，2014，39（1）：126-130.

[6]ElMassalamia M， Palatnik-de-Sousa I， Areiza M C L，et al.On the magnetic anisotropy of super duplex stainless steel[J].Journal of Magnetism and Magnetic Materials,2011,32(3):2403-2407.

[7]徐乃龙, 王利, 洪继要,等.Nb-Ti微合金碳氮化物析出行为及微合金钢性能研究[J]. 锻压技术,2014,39(5):121-125.

Xu N L，Wang L，Hong J Y，et al.Study on performance of carbonitride precipitation and properties in Nb-Ti microalloyed steels[J]. Forging & Stamping Technology,2014,39(5):121-125.

[8]Tavares S, Silva M D, Pardal J, et al. Microstructural changes produced by plastic deformation in the UNS S31803 duplex stainless steel[J]. Journal of Materials Processing Technology，2006,180(1)：318-322.

[9]徐兰兰.1J50合金磁性能和尺寸稳定性优化工艺及机理的研究[D].哈尔滨：哈尔滨工业大学，2013.

Xu L L.Study on the Optimized Process and Mechanism of 1J50 Alloy Magnetic Proeties and Dimensional Stability[D].Harbin：Harbin Institute of Technology,2013.

[10]潘秋红, 董则防, 黄瑶,等.均匀化退火对纯铝铸轧-冷轧板各向异性的影响[J]. 锻压技术, 2009, 33(6): 128-131.

Pan Q H, Dong Z F, Hang Y， et al. Influence of homogenizing annealing on anisotropy of aluminum sheet with roll-casting and cold rolling[J]. Forging & Stamping Technology，2008,33(6):128-131

[11]张文康，广红兵，姜世勇，等.无取向硅钢组织结构和化学成分对磁性能影响及生产工艺控制[J] .太钢科技，2005，(1):1-13.

Zhang W K, Guang H B,Jiang S Y, et al. Effect on magnetic properties of nonoriented silicon steel structure and chemical composition on and the control of production process[J]. Taigang Science and Technology，2005，(1):1-13.

[12]于宏，田素贵，耿新，等.冷变形CrMo钢系列温度退火后的组织与性能[J].沈阳工业大学学报，2001,23(6):459-462.

Yu H, Tian S G, Geng X, et al.Structure and properties of CrMo steel annealed in series of temperatures after cool deformation[J]. Journal of Shenyang University of Technology，2001,23(6):459-462.

[13]喻兰英，罗宏，李新跃.退火对 2205双相不锈钢-16MnR爆炸复合板性能的影响[J].金属热处理，2010，35(3):51-53.

Yu L Y, Luo H, Li X Y. Effect of annealing process on properties of explosive clad plates of 2205 duplex stainless steel-16MnR[J].Heat Treatment of Metals,2010，35(3):51-53.

[14]曹光明.退火对软磁合金的最大磁导率影响的机理研究[J].潍坊高等专科学校学报，2000，(1):41-42.

Cao G M. Study on mechanisms of the effect of anneating on maximum permeability of soft magnetic alloy[J]. Journal of Weifang College,2000，(1):41-42.

[15]张沛学，任学平，谢建新，等.σ相对双相不锈钢低温超塑性的影响[J].锻压技术，2003，28(2): 38-40.

Zhang P X, Ren X P, Xie J X, et al. Effect of phase on superplasticity of duplex stainless steel in lower temperature[J]. Forging & Stamping Technology，2003,28(2):38-40.

[16]Palit Sagar S， Ravi Kumar B， Dobmann G，et al.Magnetic characterization of cold rolled and aged AISI 304 stainless steel[J].NDT & E International， 2005，38:674-681.

[17]宋瑞宁，朱伟，刘恩克，等.内应力对Mn2NiGa铁磁形状记忆合金的结构、相变和磁性能的影响[J].物理学报，2012,61(2):1-6.

Song R N, Zhu W, Liu E K, et al. Effect of internal stress on structure,martensitic transformation and magnetic properties of ferromagnetic shape memory alloy Mn2NiGa[J].Acta. Phys. Sin.,2012，61(2):1-6.

服务与反馈：

【文章下载】【加入收藏】