一种改进的损伤断裂准则及其在板料成形中的应用

英文标题：An improved damage fracture criterion and its application in sheet metal forming

作者：曾嵘黄亮李建军洪秀冬

单位：华中科技大学

分类号：TG304

出版年,卷(期):页码：2015,40(8):13-19

摘要：

将Lemaitre损伤断裂准则中的单轴应力状态的线性损伤修正为多轴应力状态的非线性损伤，并以铝合金5052-O筒形件冲压实验为例，揭示了工件的等效应力、等效塑性应变和单位体积损伤值分布规律，分析了模拟和试验成形件深度和壁厚的相对误差，用于评估改进的Lemaitre损伤断裂准则在板料成形工艺中的适用性。结果表明：在使用了改进的Lemaitre损伤断裂准则的筒形件冲压模拟中，工件的等效应力和等效塑性应变的最大值都出现在圆板与凸模圆角接触的区域，且材料的单位体积损伤值达到1的区域发生了破裂。采用改进的Lemaitre损伤断裂准则预测得到的成形深度误差和壁厚最大误差分别仅为6.5%和9.2%。

The linear damage under uniaxial stress state in the Lemaitre damage fracture criterion was amended as the nonlinear damage under multi-axis stress states, and the cylindrical stamping experiment of aluminum alloy 5052-O was set as an example. The distribution regularity of the equivalent stress, the equivalent plastic strain and the damage per volume were revealed. The relative errors of the forming depth and the wall thickness in simulations and experiments were analyzed, which were used to evaluate applicability of the modified Lemaitre damage fracture criterion in the sheet metal forming process. The results show that the maximum values of the equivalent stress and the equivalent plastic strain appear at the contact area of the circular plate and the punch when the modified Lemaitre damage fracture criterion is used in the simulations of cylindrical stamping process. Furthermore, stamping parts occur fracture at where the damage value per volume reaches 1. The relative error of the forming depth and the maximum relative error of the wall thickness predicted by the modified Lemaitre damage fracture criterion are only 6.5% and 9.2%, respectively.

基金项目：

国家自然科学基金资助项目（51105042）；中央高校基本科研业务费资助项目（2012QN040）

曾嵘（1992-），男，博士研究生黄亮（1981-），男，博士，副教授

参考文献：

［1］虞松, 陈军, 阮雪榆. 韧性断裂准则与试验和理论研究[J]. 中国机械工程，2006, 17(19): 2049-2052.Yu S, Chen J, Ruan X Y. Experimental and theoretical research on ductile fracture criterion[J]. China Mechanical Engineering, 2006, 17(19): 2049-2052.
［2］Camacho G T, Ortiz M. Computational modelling of impact damage in brittle materials[J]. International Journal of solids and structures, 1996, 33(20): 2899-2938.
［3］Rice J R, Tracey D M. On the ductile enlargement of voids in triaxial stress fields[J]. Journal of the Mechanics and Physics of Solids, 1969, 17(3): 201-217.
［4］黄建科, 董湘怀. 金属成形中韧性断裂准则的细观损伤力学研究进展[J].上海交通大学学报, 2006, 40(10): 1748-1753.Huang J K, Dong X H. Research progress of micro-macro damage mechanics for ductile fracture criterion in metal forming [J]. Journal of Shanghai Jiaotong University, 2006, 40(10):1748-1753.
［5］Lemaitre J. A continous damage mechanics model for ductile fracture[J], Journal of Engineering Materials and Technology, 1985, 107(1): 83-89.
［6］Lee S W, Pourboghrat F. Finite element simulation of the punchless piercing process with Lemaitre damage model[J]. International Journal of Mechanical Science, 2005, 47(11): 1756-1768.
［7］于忠奇, 杨玉英, 王永志, 等. 基于韧性断裂准则的铝台金板材成形极限预测[J]. 中国有色金属学报, 2003, 13(5): 1223-1226. Yu Z Q, Yang Z Y, Wang Y Z, et al. Application of ductile fracture criterion to prediction of forming limit in aluminum alloy sheet forming [J]. The Chinese Journal of Nonferrous Metals, 2003, 13(5):1223-1226.
［8］吴卷, 詹梅, 蒋华兵, 等.一种改进的Lemaitre韧性断裂准则及其在旋压成形中的应用[J].航空学报,2011,32(7):1309-1317.Wu J, Zhan M, Jiang H B, et al. A modified Lemaitre ductile fracture criterion and its application to spinning forming [J].Journal of Aviation, 201l, 32(7): 1309-1317.
［9］王光艳,梅益,陈浪, 等. 42CrMo环件轧制成形的数值模拟与分析[J].锻压技术,2014,39(5):82-86.Wang G Y, Mei Y, Chen L, et al. Analysis and numerical simulation on ring rolling of 42CrMo[J]. Forging & Stamping Technology, 2014, 39(5): 82-86.
［10］陈志英,董湘怀. GTN细观损伤模型参数对板料损伤行为的影响[J].锻压技术,2012, 37(3): 23-27.Chen Z Y, Dong X H. Influence of GTN meso-damage model for parameters on sheet forming damage behavior [J]. Forging & Stamping Technology, 2012, 37(3): 23-27.
［11］周敏. 5CrNiMo热环轧芯辊断裂失效分析[J].锻压技术，2015,40(5):145-148.Zhou M. Failure analysis on the fracture of hot ring-rolling core roller 5CrNiMo[J]. Forging & Stamping Technology, 2015,40(5):145-148.
［12］东赟鹏, 王超渊, 宋晓俊, 等. GH5188合金流变行为研究[J]. 锻压技术, 2013, 38(6): 116-121.Dong Y P, Wang C Y, Song X J, et al. Study on plastic deformation behavior of GH5188 superalloy [J]. Forging & Stamping Technology, 2013, 38(6): 116-121.
［13］刘先兰, 张文玉, 刘楚明. 细观损伤力学及其在金属塑性加工中的应用[J]. 锻压技术, 2008, 33(1): 9-13.Liu X L, Zhang W Y, Liu C M. Meso damage mechanics and its application in metal plastic forming[J]. Forging & Stamping Technology, 2008, 33(1): 9-13.
［14］GB/T 228.1—2010, 金属材料拉伸试验第1部分: 室温试验方法[S].GB/T 228.1—2010, Metallic materials—Tensile testing—Part 1: Method of test at room temperature[S].

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】