采用商业有限元软件ABAQUS，建立了管材液压成形有限元模型，分别在非脉动和脉动液压加载下对管材液压成形过程进行了有限元仿真，并通过试验对有限元模型进行了验证。研究结果表明：在不同脉动液压振幅和频率加载下，接触压强均小于液体压强，而且随着管材的胀形，接触压强逐渐接近液体压强，当胀形结束时，接触压强与液体压强的差值为20%左右；脉动液压振幅越大及频率越高，则接触压强波动也越大；脉动液压振幅越大，接触压强越接近液体压强，但在脉动液压频率大小合适时，接触压强最接近液体压强。

The finite element model of tube hydroforming was established by the commercial software ABAQUS，and the FE simulations under non-pulsating and pulsating pressures were conducted. The finite element model was verified through tests. The results show that the contact pressure is always less than the hydraulic pressure under different pulsating hydraulic amplitudes and frequencies, and it gradually approaches the hydraulic pressure with the tube bulging. When the tube finishes bulging, the difference between them is about 20%. The larger the pulsating hydraulic amplitude and the frequency are, the higher the fluctuation of the contact pressure is and the closer the contact pressure is to the hydraulic pressure. When the frequency is suitable, the contact pressure is closer to the hydraulic pressure.

基金项目：

广西自然科学基金资助项目(2013GXNSFAA019305)；制造系统与先进制造技术广西重点实验室基金项目(14-045-15-005Z)

何玉林（1980－），女，硕士，讲师

参考文献：

[1]陈仙风,苏海波,徐小华.液压成形汽车吸能盒研制关键技术[J]. 塑性工程学报,2014,21(2):46-50.

Chen X F, Su H B, Xu X H.Key technologies of hydroforming automobile crash box [J]. Journal of Plasticity Engineering, 2014,21(2):46-50.

[2]康万平, 王宇, 康蕾. 管件液压成型技术简述 [J]. 焊管, 2010, 33(1): 53-55.

Kang W P, Wang Y, Kang L. Introduction of pipe fitting hydroform technology [J]. Welding Pipe and Tube, 2010, 33(1): 53-55.

[3]王宁华，杨连发. 基于液压胀形实验及增量理论构建管材本构关系[J]. 锻压技术,2015,40(2):133-137.

Wang N H, Yang L F. Determination of constitutive relationship of tubular materials based on incremental theory and hydraulic bulge test [J]. Forging & Stamping Technology, 2015,40(2):133-137.

[4]刘亚秀，刘雅芳，姜艳梅，等.TA15钛合金热加工工艺参数与抗拉强度定量关系的神经网络分析[J]. 稀有金属, 2013, 37(6): 876-882.

Liu Y X, Liu Y F, Jiang Y M, et al. Neural network analysis of quantitative relationship between hot-process parameters and tensile strength of TA15 Ti alloys[J].Chinese Journal of Rare Metals, 2013, 37(6): 876-882.

[5]杨素媛,钟红然，陶逸诗，等.稀土镁合金搅拌摩擦焊接接头组织及性能分析[J].稀有金属, 2013, 37(1): 33-37.

Yang S Y, Zhong H R, Tao Y S, et al. Microstructure and properties of friction stir welded joints of magnesium rare earth alloy[J]. Chinese Journal of Rare Metals, 2013, 37(1): 33-37.

[6]张帆, 郎利辉, 程鹏志, 等. 异形截面构件多工序充液成形工艺及过程优化[J]. 锻压技术, 2014, 39 (3):42-46.

Zhang F，Lang L H，Cheng P Z，et al. Research on multi-step hydroforming process and optimization of process parameters for profiled cross-section component [J]. Forging & Stamping Technology, 2014, 39 (3):42-46.

[7]吴春蕾, 杨连发. 管材液压成形中表面粗糙度与液体压强对摩擦系数的影响[J]. 锻压技术,2014,39(11):74-80.

Wu C L, Yang L F. Effects of surface roughness and hydraulic pressure on friction coefficient in tube hydroforming [J]. Forging & Stamping Technology, 2014,39(11):74-80.

[8]Yi H K, Yim H S, Lee G Y, et al. Experimental investigation of friction coefficient in tube hydroforming [J]. Transactions of Nonferrous Metals Society of China, 2011, 21: 194-198.

[9]Vollersten F, Prange T, Sander M. Hydroforming：needs，developments and perspectives[J] .Advanced Technology of Plasticity, 1999, 2:1197-1210.

[10]刘宝胜，吴为，曾元松，等. TC2管材超塑性变形行为[J]. 锻压技术，2014，39（4）：122-125.

Liu B S，Wu W，Zeng Y S，et al. Study on superplastic behavior of TC2 extrusion tube [J]. Forging & Stamping Technology，2014，39（4）：122-125.

服务与反馈：

【文章下载】【加入收藏】