球形封头热冲压成形残余应力分析

英文标题：Residual stress analysis of hot stamping for spherical head

分类号：

出版年,卷(期):页码：2016,41(4):14-19

摘要：

球形封头在其直边段易发生折皱和开裂，残余应力过大是造成其缺陷的根本原因之一。针对无损X射线衍射法、有损全释放法这两种残余应力测试方法的检测原理、测试方法及应用特点等方面进行了分析介绍。以12Cr2Mo1R（H）材料为例，采用两种方法分别测量了球形封头热冲压成形后的外壁残余应力值。揭示了封头外壁残余应力分布规律：封头外壁的残余应力值由底部开始逐渐增大，过渡段为应力值转折区域，进入直边段后，残余应力值达到最大。通过对比发现：两种测量方法测得的残余应力变化规律相似；全释放法测得的残余应力值较大；残余应力值在封头外壁直边段部分达到最大。

Wrinkling and cracking easily happen in the straight part of spherical head, and one of the essential reasons is the excessive residual stress. It was introduced and analyzed the principle，procedure and application characteristics of undamaged X-ray diffraction method and damaged full release method. For material 12Cr2Mo1R(H)，the outer wall residual stress after hot stamping for spherical head was studied by the above methods. The residual stress distribution rule of outer wall of head was revealed: the residual stress values of head outer wall increased gradually from the bottom. The transition section was the transition area of stress value. After entering straight section, the residual stress reached the maximum value. The results show that the residual stress changing rules are the same by two methods of measurement, the residual stress values by full release method are bigger, the residual stress values achieve the maximum value in the straight section of the head outer wall.

基金项目：

国家自然科学基金资助项目（51304186）

邓晓婷（1987-），女，博士研究生

参考文献：

[1]朱向哲，谢禹均，王晓华. 半球形后壁封头冲压成形有限元分析及优化[J]. 辽宁石油化工大学学报，2004,24（4）：51-53.

Zhu X Z, Xie Y J, Wang X H. Finite element analysis and optimization of the drawing process of head with thick semi-spherical shell [J].Journal of Liaoning University of Petroleum & Chemical Technology, 2004,24（4）：51-53.

[2]陈帅峰，王守东，雷玉川，等.大型厚壁椭圆封头多次热冲压成形分析[J]. 锻压技术，2015，40（2）：37-40.

Chen S F，Wang S D，Lei Y C, et al. Analysis of multi-hot stamping forming for large thick-wall ellipse head [J]. Forging & Stamping Technology，2015，40（2）：37-40.

[3]肖元超，杨尚斌，张明哲，等. 不锈钢封头典型裂纹原因分析及修复[J]. 热处理技术与装备，2012, 33（1）：42-45.

Xiao Y C, Yang S B, Zhang M Z, et al. Reason analysis and repairation of typical crack of stainless steel head [J]. Heat Treatment Technology and Equipment, 2012, 33（1）：42-45.

[4]Adnen Laamouri, Habib Sidhom, Chedly Braham. Evaluation of residual stress relaxation and its effect on fatigue strength of AISI 316L stainless steel ground surfaces: Experimental and numerical approaches[J]. International Journal of Fatigue, 2013,48:109-121.

[5]梁方杰. 不锈钢椭圆封头热压制裂纹分析[J]. 石油化工设备，2005, 34（3）：65-67.

Liang F J. Cracking analysis on hot formed stainless steel elliptical head [J]. Petrochemical Equipment, 2005, 34（3）：65-67.

[6]朱晓波. 奥氏体不锈钢冷冲压椭圆形封头塑性变形预测及检测方法研究[D]. 杭州：浙江大学，2014.

Zhu X B. Research on Prediction and Test Method of Plastic Deformation for Cold Stamping Formed Elliptical Head Made of Austenitic Stainless Steel [D]. Hangzhou: Zhejiang University, 2014.

[7]王庆明，孙渊. 残余应力测试技术的进展与动向[J]. 机电工程，2011,28（1）：11-15.

Wang Q M, Sun Y. Research development on the test methods of residual stress [J]. Journal of Mechanical & Electrical Engineering, 2011,28（1）：11-15.

[8]蒋刚，谭明华，王伟明，等. 残余应力测量方法的研究现状[J]. 机床与液压，2007, 35（6）：213-216.

Jiang G, Tan M H, Wang W M, et al. Present research status of measuring residual stress [J]. Machine Tool & Hydraulics, 2007, 35（6）：213-216.

[9]蒋玉善. 热处理工艺对12Cr2Mo1R钢的组织和性能影响[J]. 山东冶金，2013, 35（4）：34-36.

Jiang Y S. Effects of heat treatment process on the microstructure and mechanical properties of 12Cr2Mo1R steel [J]. Shandong Metallurgy, 2013, 35（4）：34-36.

[10]Jozsef Szalai, Ferenc Papp. A new residual stress distribution for hot-rolled I-shaped sections[J]. Journal of Constructional Steel Research, 2005,61:845-861.

[11]陈会丽，钟毅，王华昆，等残余应力测试方法的研究进展[J]. 云南冶金，2005, 34（3）:52-54.

Chen H L, Zhong Y, Wang H K, et al. Research progress of the method for residual stress measurement [J]. Yunnan Metallurgy, 2005, 34（3）:52-54.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】