第二级固溶温度对7050铝合金组织和性能的影响

英文标题：Influence of the second stage solution temperature on microstructure and properties of aluminum alloy 7050

作者：刘浩肖铁忠黄娟高静

单位：四川工程职业技术学院

分类号：TG146.2

出版年,卷(期):页码：2016,41(6):142-145

摘要：

为了研究双级固溶、双级时效处理下的固溶温度对7050铝合金的影响，采用常温拉伸、晶间腐蚀等方法研究了双级固溶、双级时效热处理制度下第二级固溶温度对7050铝合金组织和性能的影响。结果表明，随着第二级固溶温度的升高合金晶粒尺寸逐渐长大，残余第二相不断固溶。495 ℃时的S相基本固溶，残余第二相体积分数为0.19%，晶粒尺寸较小，合金屈服强度ReL为655 MPa，抗拉强度Rm为694 MPa，伸长率A50 mm为14.40%，综合力学性能最好。温度过高时合金发生过烧，性能减弱。晶间腐蚀从合金外部晶界开始向内部扩展，耐晶间腐蚀性能随着残余第二相的逐渐固溶而增强。

In order to research the influence of solid solution temperature on aluminum alloy 7050 under two-stage solution and two-stage aging, the effect of the second levels solid solution temperature on microstructure and properties of aluminum alloy 7050 with two-stage solution and two-stage aging heat treatment was studied by tensile test and intergranular corrosion. The results show that the grain size of the alloy increases gradually with the increase of the second levels solid solution temperature, and solid solution of the second phase continues. At temperature of 495℃, the S plase is solid soluted basically, volume fraction of the residual second phase particles is 0.19%, and grain size is smaller with alloy ReL(yield strength) is 655 MPa, Rm(tensile strength) is 694 MPa, A50 mm(elongation) is 14.40%, which shows the best comprehensive performance. When the temperature is too high, alloy performance weakens because of the over burning. The beginning of intergranular corrosion extends from the outer grain boundary of alloy to inner of the grain, and the corrosion resistance of the alloy increases with the decrease of the residual second phase.

基金项目：

基金项目:垫江县汽摩配套产业发展分析与研究项目（CSTC2013JCCXB60001）

作者简介：刘浩（1988-），男，硕士，助教 E-mail：464320329@qq.com 通讯作者：肖铁忠（1986-），男，硕士，助教 E-mail：593712861@qq.com

参考文献：

［1］Mazzer E M, Afonso C R M, Bolfarini C, et al. Microstructure study of Al 7050 alloy reprocessed by spray forming and hot-extrusion and aged at 121 ℃[J]. Intermetallics,2013, 43: 182-187.

［2］Li J, Li F G, Xue F M, et al. Micro-mechanical behavior study of forged 7050 aluminum alloy by micro-indentation [J]. Materials and Design, 2012, 37: 491-499.

［3］李杰,宋仁国,陈小明，等.固溶处理对7050高强铝合金显微组织和机械性能的影响[J].稀有金属,2009,33(4): 494-499.Li J, Song R G, Chen X M, et al. Effects of solid solution treatment on microstructure and mechanical properties of 7050 high strength aluminum ally [J]. Chinese Journal of Rare Metal, 2009, 33(4): 494-499.

［4］宋丰轩,张新明,刘胜胆,等.固溶制度对7050铝合金微观组织和腐蚀性能的影响[J].航空材料学报,2013,33(4):14-21.Song F X, Zhang X M, Liu S D, et al. Effects of solution heat treatment on microstructure and corrosion properties of 7050 Al Alloy[J].Journal of Aeronautical Materials, 2013, 33(4): 14-21.

［5］Chen K H, Liu H W, Zhang Z, et al. The improvement of constituent dissolution and mechanical properties of 7055 aluminum alloy by stepped heat treatments [J]. Journal of Materials Processing Technology, 2003, 142(1): 190-196.

［6］熊创贤,邓运来,万里,等. 7050铝合金板在固溶过程中微结构与织构的演变[J].中国有色金属学报, 2010, 20(3): 427-434.Xiong C X, Deng Y L, Wan L, et al. Evolutions of microstructures and textures of 7050 Al alloy plate during solution heat treatment [J]. The Chinese Journal of Nonferrous Metals, 2010, 20(3): 427-434.

［7］王春光,王东哲,万红,等.锻造及热处理工艺对 GH4169合金组织与性能的影响[J].锻压技术,2014,39(12):14-18.Wang C G, Wang D Z, Wang H, et al. Influence of forging and heat treatment on structure property of GH4169 alloy [J]. Forging & Stamping Technology, 2014, 39(12):14-18.

［8］GB/T 228.1—2010, 金属材料拉伸试验第1部分:室温试验方法[S].GB/T 228.1—2010, Metallic materials-tensile testing -Part 1: Method of test at room temperatures[S].

［9］Li X M，Starink M J . The effect of compositional variations on characteristics of coarse intermetallic particles in overaged 7XXX Al alloys[J].Materials Science and Technology, 2001,17(11): 1324-1328.

［10］Wang T, Yin Z M, Sun Q. Effect of homogenization treatment on microstructure and hot workability of high strength 7B04 aluminium alloy [J]. Transactions of Nonferrous Metals Society of China, 2007, 17(2): 335-339.

［11］Li N K, Cui J Z. Microstructural evolution of high strength 7B04 ingot during homogenization treatment [J]. Transactions of Nonferrous Metals Society of China, 2008, 18(4): 769-773.

服务与反馈：

【文章下载】【加入收藏】