双相镁锂合金正挤压有限元模拟与实验分析

英文标题：Numerical simulation and experimental research on direct extrusion for dual-phase magnesium lithium alloy

作者：姜炳春王淑萍刘方方唐联耀李真真

单位：广东科技学院

分类号：TG376

出版年,卷(期):页码：2017,42(1):116-120

摘要：

以LZ92镁锂合金为研究对象，采用Deform-3D软件对其正挤压变形方式进行数值模拟。研究了不同挤压比（分别为10，20和30）对等效应力和等效应变的影响。结合正挤压变形的分析结果进行热挤压实验，对变形后的试样进行显微组织观察和力学性能测试。结果表明：随着挤压比的增大，试样的等效应变增大，均匀性增强，等效应变以0.5的增长速度线性增长，最大等效应变高达3；LZ92镁锂合金再结晶越充分，晶粒细化越明显，晶粒尺寸由45 μm细化至约15 μm。LZ92变形镁锂合金具有优异的力学性能，随着挤压比的增大，屈服强度、抗拉强度和变形量显著提升，抗拉强度逐渐增大至203.1 MPa，较铸态提高了76%，屈服强度以40 MPa的增长速度线性增长。

For magnesium lithium alloy LZ92, the deformation mode of direct extrusion was numerically simulated by Deform-3D finite element software, and the influences of different extrusion ratios of 10, 20 and 30 on equivalent stress and equivalent strain were analyzed. According to the simulation analysis result of direct extrusion, the hot extrusion test was carried out to observe the microstructure and mechanical properties of the deformed samples. The results show that with the increase of extrusion ratio, the equivalent strain increases, and the sample homogeneity is enhanced. Therefore,the equivalent strain is in linear growth with a growth rate of 0.5, and the maximum equivalent strain is up to 3. At the same time, the more sufficient the recrystallization of magnesium lithium alloy LZ92 is, the more obvious the grain refinement is, and the grain size is refined from 45 μm to 15 μm. LZ92 deformation magnesium lithium alloy has excellent mechanical properties. With the increase of extrusion ratio, the yield strength, tensile strength and deformation significantly increase. The tensile strength gradually increases to 203.1 MPa which is 76% more than the cast state, and the yield strength grows linearly at a speed of 40 MPa.

基金项目：

广东省青年创新人才类项目（2015KQNCX192）；广东科技学院重点项目（GKY-2015KYZD-3)；广东科技学院一般项目（GKY-2015KYYB-9）

姜炳春（1987-），男，硕士 E-mail：jiangbingchun_2008@163.com

参考文献：

[1]Zhang H H, Huang G S, Li J H, et al. Influence of warm pre-stretching on microstructure and properties of AZ31 magnesium alloy [J]. Journal of Alloys and Compounds, 2013, 563(9): 150-154.

[2]Xiu L H, Yan L, Peng L, et al. Hot deformation behavior and microstructure evolution of a Mg-Gd-Nd-Y-Zn alloy[J]. Rare Metals, 2016, 35（7）: 532-536.

[3]Hu G S, Zhang D F, Zhao D Z, et al. Microstructures and mechanical properties of extruded and aged Mg-Zn-Mn-Sn-Y alloys [J]. Transactions of Nonferrous Metals Society of China, 2014, 24(10): 3070-3075.

[4]陈斌, 冯林平, 钟皓, 等. 变形Mg-Li-Al-Zn合金的组织与性能[J]. 北京航空航天大学学报, 2004, 30(10): 976-979.

Chen B, Feng L P, Zhong H, et al. Microstructures and properties of a Mg-Li-Al-Zn wrought alloy[J]. Journal of Beijing University of Aeronautics and Astronautics, 2004, 30(10): 976-979.

[5]王涛, 张密林, 牛中毅, 等. Mg-Li-Al-Zn-RE合金铸态和退火态的组织与性能[J]. 金属热处理, 2008, 33(2): 5-8.

Wang T, Zhang M L, Niu Z Y, et al. Microstructure and proper-ties of the as-cast and annealing Mg-Li-Al-Zn-RE alloys[J]. Heat Treatment of Metals, 2008, 33(2): 5-8.

[6]冯林平, 陈斌, 钟皓, 等. β基Mg-12Li-3Al-5Zn合金的塑性变形行为[J]. 金属热处理, 2005, 30(3): 36-39.

Feng L P, Chen B, Zhong H, et al. Plastic deformation behaviors of β based Mg-12Li-3Al-5Zn alloy[J]. Heat Treatment of Metals, 2005, 30(3): 36-39.

[7]Yan H, Chen R S, Han E H. Microstructures and mechanical properties of cold rolled Mg-8Li and Mg-8Li-2Al-2RE alloys [J]. Transactions of Nonferrous Metals Society of China, 2010, 20(S2): 550-554.

[8]刘天模, 刘建忠, 卢立伟, 等. 双向双通道变通径挤压AZ31镁合金的显微组织及变形行为[J]. 中国有色金属学报, 2010, 20(9): 1657-1664.

Liu T M, Liu J Z, Lu L W, et al. Microstructure and deformation behavior of dual-directional extruded AZ31 magnesium alloy[J].The Chinese Journal of Nonferrous Metals, 2010, 20(9): 1657-1664.

[9]Kolleck R, Veit R, Merklein M, et al. Investigation on induction heating for hot stamping of boron alloyed steels [J]. CIRP Annals-Manufacturing Technology, 2009, 58(1): 275-278.

[10]Hoffmann H, So H, Steinbeiss H. Design of hot stamping tools with cooling system [J]. CIRP Annals -Manufacturing Technology, 2007, 56 (1):269-272.

[11]吴利斌, 孟祥瑞, 崔崇亮, 等. 超轻变形Mg-Li-Al-Zn合金的显微组织和性能[J]. 铸造技术, 2009, 30(10): 1256-1259.

Wu L B, Meng X R, Cui C L, et al. Microstructure and mechanical properties of super light deformation Mg-Li-Al-Zn alloy[J]. Casting Technique, 2009, 30(10): 1256-1259.

[12]Xu T C, Peng X D, Jiang J W, et al. Effect of Sr content on microstructure and mechanical properties of Mg-Li-Al-Mn alloy[J]. Transactions of Nonferrous Metals Society of China, 2014, 24 (9): 2752-2760.

[13]李瑞红,蒋斌,吴立斌,等. 超轻Mg-Li-Al系变形镁合金挤压板材的组织及性能[J]. 中国有色金属学报, 2016, 26(1): 31-36.

Li R H, Jiang B, Wu L B, et al. Microstructure and mechanical properties of as-extruded ultra-light Mg-Li-Al sheet[J]. The Chinese Journal of Nonferrous Metals，2016, 26(1): 31-36.

[14]崔崇亮, 刘旭贺, 吴立斌，等. 挤压变形态Mg-5Li-3Al-2Zn-x Y合金的显微组织和力学性能[J]. 稀有金属材料与工程,2013, 42(1): 89-93.

Cui C L, Liu X H, Wu L B, et al. Microstructure and mechanical properties of as-extruded Mg-5Li-3Al-2Zn-x Y alloy[J]. Rare Metal Materials and Engineering, 2013, 42(1): 89-93.

[15]贾玉鑫, 黄金亮, 冯剑. Mg-8Li-2Al-1Zn合金的热变形行为[J]. 材料热处理学报, 2014, 35(9): 210-214.

Jia Y X, Huang J L, Feng J. Hot deformation behavior of Mg-8Li-2Al-1Zn alloy[J]. Transactions of Materials and Heat Treatment, 2014, 35(9): 210-214.

[16]ASTM E 8，Standard test methods for tension testing of metallic materials[S].

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】