焊合角和焊合室深度对复杂悬臂空心铝型材挤压成形质量的影响

英文标题：Influences of welding angle and welding chamber depth on the extrusion quality of hollow aluminum profile with complex cantilever

作者：曾文浩魏刚邓小亮陈功

单位：西华大学

关键词：长悬臂铝型材挤压焊合角焊合室深度数值模拟

分类号：TG376

出版年,卷(期):页码：2017,42(6):92-100

摘要：

应用HyperXtrude有限元分析软件，考察了带长悬臂结构空心截面铝型材挤压时的焊合角α和焊合室深度h对其挤压成形质量的影响。结果表明：当α在15°~45°时，型材悬臂处及空心部位四周分流桥下金属的流动速率较大，开始焊合的时间早，焊合历程长；当α增加到60°时，相应区域金属的流动速率明显降低，焊合推迟；在α达到90°时，该情况最为严重，焊合历程变短。α为45°时，模芯最大偏移量达到最小值0.045 mm。随着h的增加，焊合面静水压力最小值与上模最大等效应力及模芯最大偏移量均逐渐增大。综合考虑各因素的影响，确定该型材挤压模具的最佳焊合角和焊合室深度分别为45°与20 mm，并将其用于挤压模具设计，试模发现模拟结果与试模结果吻合较好，挤出型材的综合质量较高。

Based on finite element analysis software HyperXtrude, the influences of welding angle α and welding chamber depth h on extrusion forming quality for a hollow section aluminum profile with long cantilever structure were investigated. The results indicate that the metal flow velocity under port bridges around profile cantilever and hollow section is high, and the metal welding starts early and has a long time when α ranges from 15° to 45°. Then, the metal flow velocity of corresponding region decreases obviously and the metal welding delays when α is up to 60°. While it becomes the most serious when α increases to 90°, and the metal welding time becomes short. Meanwhile, the maximum offset of mandrel reaches the minimum values 0.045 mm when α is 45°. Furthermore, the minimum hydrostatic pressure on the welding plane, the maximum equivalent stress of upper die and the
maximum offset of mandrel have the similar incremental trends with the increase of welding depth h. The optimal welding angle of 45° and welding chamber depth of 20 mm were determined by considering influences of each factor comprehensively. According to the optimal scheme, the extrusion die is designed. It is found that the simulation results and the experimental results fit well by extrusion trial, and the comprehensive quality of the extruded profile is high.

基金项目：

四川省科技支撑计划项目(16201401)

曾文浩(1991-)，男，硕士研究生魏刚(1971-)，男，博士，教授

参考文献：

［1］雷步芳, 岳峰, 李永堂,等. 铝及铝合金挤压工艺及设备[M]. 北京：国防工业出版社, 2014.

Lei B F, Yue F, Li Y T, et al. Extrusion Process and Equipment for Aluminum and Its Alloys[M]. Beijing：National Defence Industry Press, 2014.

［2］黄东男, 张志豪, 李静媛,等. 焊合室深度及焊合角对方形管分流模挤压成形质量的影响[J]. 中国有色金属学报, 2010, 20(5):954-960.

Huang D N, Zhang Z H, Li J Y, et al. Influences of welding chamber depth and welding angle on forming quality of extrusion of square tube by porthole die[J]. The Chinese Journal of Nonferrous Metals, 2010, 20(5):954-960.

［3］吴向红, 赵国群, 孙胜,等. 分流组合模挤压过程数值模拟及模具应力分析[J]. 中国机械工程, 2006,17(S1):115-118.

Wu X H, Zhao G Q, Sun S, et al. Porthole die extrusion process numerical simulation and die stress analysis [J]. China Mechanical Engineering, 2006,17(S1):115-118.

［4］程磊, 谢水生, 黄国杰,等. 焊合室高度对分流组合模挤压成形过程的影响[J]. 稀有金属, 2008, 32(4):442-446.

Chen L, Xie S S, Huang G J, et al. Effects of height of welding chamber heights on extrusion forming process of porthole die[J]. Chinese Journal of Rare Metals, 2008, 32(4):442-446.

［5］Lee J M, Kim B M, Kang C G. Effects of chamber shapes of porthole die on elastic deformation and extrusion process in condenser tube extrusion[J]. Materials & Design, 2005, 26(4):327-336.

［6］Chen H, Zhao G Q, Zhang C S, et al. Effects of multistep welding chamber on extrusion product quality and die strength[J]. Applied Mechanics & Materials, 2010, 44-47:311-315.

［7］徐永礼, 黄双健, 庞祖高,等. 圆管铝型材挤压模具失效分析及其热处理工艺优化[J]. 锻压技术, 2015, 40(2):116-122.

Xu Y L, Huang S J, Pang Z G, et al. Failure analysis and optimization of heat treatment process for aluminum profile extrusion die[J]. Forging & Stamping Technology, 2015, 40(2):116-122.

［8］路帅, 王永晓, 娄淑梅,等. 基于有限元法的空心铝型材挤压过程瞬态分析[J]. 锻压技术, 2015, 40(10):130-138.

Lu S, Wang Y X, Lou S M, et al. Analysis on transient extrusion process of hollow aluminum profile based on finite element method [J]. Forging & Stamping Technology, 2015, 40(10):130-138.

［9］纵荣荣, 郝秋红, 韩志君,等. 轨道车辆用超宽幅薄壁铝型材挤压过程数值模拟及模具优化[J]. 塑性工程学报, 2015, 22(4):39-43.

Zong R R, Hao Q H, Han Z J, et al. Numerical simulation of extrusion and die optimization for super wide thinwalled aluminum profile for railwway vehicles[J]. Journal of Plasticity Engineering, 2015, 22(4):39-43.

［10］钟建华, 袁志燕, 刘艳霞. 基于Altair HyperXtrude的空心铝型材挤压成型仿真模拟[J]. 上海有色金属, 2015, 36(4):167-172.

Zhong J H, Yuan Z Y, Liu Y X. The numerical simulation of solid aluminum profile extrusion based on Altair HyperXtrude[J]. Shanghai Nonferrous Metals, 2015, 36(4):167-172.

［11］Altair HyperXtrude 13.0 User Guide
［Z］. Shanghai: Altair Engineering, 2014.

［12］Lof J, Blokhuis Y. FEM simulations of the extrusion of complex thinwalled aluminium sections [J]. Journal of Materials Processing Technology, 2002, 122(2):344-354.

［13］刘静安, 邵莲芬. 铝合金挤压工模具典型图册[M]. 北京：化学工业出版社, 2008.

Liu J A, Shao L F. Typical Atlas of Extrusion Tool and Die for Aluminum Alloys[M]. Beijing：Chemical Industry Press, 2008.

［14］Akeret R. Properties of pressure welds in extruded aluminum alloy sections[J]. Journal Institute of Metals, 1972, 10:202-207.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】