盘形件旋压对称增厚成形工艺

英文标题：Spinning process on symmetrical thickening of disk-like parts

作者：王炜金俊松王新云邓磊

单位：华中科技大学

分类号：TG381

出版年,卷(期):页码：2017,42(10):73-80

摘要：

针对薄辐板厚轮缘盘形件的旋压对称增厚成形工艺进行了研究，分析了旋压对称增厚成形的原理。基于Simufact.forming软件设计了有限元模拟方案，分析了旋压对称增厚成形的变形过程、成形载荷和失效形式，研究了极限增厚时各工艺参数对型槽充型能力、坯料弯曲程度和成形形态的影响规律，给出了极限弯曲程度δmax随倾角α及底部高度h的变化趋势，最后通过实验进行了验证。研究结果表明：成形过程分为均匀增厚、摆动增厚及最后充填3个成形阶段，在成形第2阶段可能出现挤出失效及折叠失效两种失效形式；极限成形时，倾角α及底部高度h值越大，型槽的充型能力越差，而γmax值越大及型槽张口程度越大，极限弯曲程度δmax越大，且可通过δmax来判定坯料的成形形态。

A spinning process on symmetrical thickening of disklike parts with both thin web plates and thickened rims was studied, and its thickening mechanism was analyzed. Then, the finite element simulation scheme was designed by software Simufact.forming, and the forming process, forming load and failure mode were analyzed. Furthermore, the influences of parameters under thickening limit on the mold filling, blank bending and forming shape were investigated, and the variations of limit bending degree δmax versus inclination angle α and bottom height h values were given. Finally, the FE analysis results were verified by experiment. The results show that the forming process can be divided into three forming stages of the uniform thickening stage, the swing thickening stage and the final filling stage. However, in the second stage, two kinds of failure modes, including extrusion and folding, occur easily. Thus, in the limit forming, the filling ability of groove decreases with the increasing of inclination angle α and bottom height h, while the larger the γmax value is and the greater the opening degree of groove is, the greater the ultimate bending degree δmax is, and the forming shape can be judged by δmax.

基金项目：

国家自然科学基金资助项目（51205144）

作者简介：王炜（1989-），男，硕士研究生，E-mail：wangweihust1989@163.com；通讯作者：金俊松（1980-），男，博士，副教授，E-mail：jsjin@hust.edu.cn

参考文献：

[1]向晓峰, 魏丽霞,马鸣图, 汽车轻量化技术的应用[J]. 汽车工程师, 2012, (5): 57-59.

Xiang X F, Wei L X, Ma M T. The application of automotive lightweight technology[J]. Auto Engineer, 2012, (5): 57-59.

[2]Merklein M, Allwood J M, Behrens B A, et al. Bulk forming of sheet metal[J]. CIRP AnnalsManufacturing Technology, 2012, 61(2):725-745.

[3]Mori K, Nakano T. Stateoftheart of plate forging in Japan[J]. Production Engineering, 2016, 10(1):81-91.

[4]Tan C J, Mori K, Abe Y. Forming of tailor blanks having local thickening for control of wall thickness of stamped products[J]. Journal of Materials Processing Technology, 2008, 202(1):443-449.

[5]赵衍璋, 金俊松, 王新云,等. 盘形件中心区域冲锻增厚工艺[J]. 锻压技术, 2016, 41(10):57-63.

Zhao Y Z, Jin J S, Wang X Y, at al. Stampingforging thickening process in the centeral area of disclike part[J]. Forging & Stamping Technology, 2016, 41 (10):57-63.

[6]郑秋, 王新云, 夏巨谌. 离合器毂体中心孔缘的冲锻成形工艺研究[J]. 锻压技术, 2011, 36(4):30-34.

Zheng Q, Wang X Y, Xia J C. Study of stampingforging hybrid forming for center hole edge of clutch hub[J]. Forging & Stamping Technology, 2011, 36(4): 30-34.

[7]Suzumura T, Mine K, Hirayama I, et al. An experimental study of new redrawing method utilizing axial compressive force and frictional force [A]. Proceedings of the 7th International Conference on Technology for Plasticity[C]. Yokohama, 2002.

[8]Abe Y, Mori K I, Ito T. Multistage stamping including thickening of corners of drawn cup [J]. Procedia Engineering, 2014, 81:825-830.

[9]Nishino S, Ohya K, Yuzawa Y. Plate forging technology by press forming[J]. Journal of the Japan Society for Technology of Plasticity, 2010, 594(51): 642-646.

[10]Jin J, Deng L, Wang X, et al. A new rotary forming process for rim thickening of a disclike sheet metal part[J]. Journal of Materials Processing Technology, 2012, 212(11):2247-2254.

[11]Kim Y J, Park J S, Cho C. Study on edge thickening flow forming using the finite elements analysis[J]. AIP Conference Proceedings, 2011, 1383: 1027-1033.

[12]Wang X, Li L, Deng L, et al. Effect of forming parameters on sheet metal stability during a rotary forming process for rim thickening[J]. Journal of Materials Processing Technology, 2015, 223:262-273.

[13]胡运展, 金俊松, 王新云, 等. 盘形件局部加热旋压增厚过程设计[J]. 塑性工程学报, 2017, 24(1):9-14.

Hu Y Z, Jin J S, Wang X Y, et al. Process design for localheating rotary thickening of disclike blanks[J]. Journal of Plasticity Engineering, 2017, 24(1):9-14.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】