齿形件精冲成形时的齿顶塌角分析及措施

英文标题：Analysis and measure on tooth crown collapse angle in fine blanking for tooth parts

作者：匡青云吕琳邓明

单位：重庆理工大学

分类号：TG381

出版年,卷(期):页码：2017,42(11):26-31

摘要：

针对精冲成形齿形件时的齿顶塌角问题，首先分析了齿形零件的几何特征及精冲成形特点，并分析了这些特征与齿形零件精冲时齿顶塌角的关系；将精冲变形区分为2个核心变形区和2个变形影响区，对核心变形区Ⅰ精冲塌角的形成过程进行了分析。然后，通过有限元模拟软件Deform-3D，找出齿顶塌角处材料在成形过程中的流动规律。结果表明：齿顶处A面轮廓附近的材料沿齿顶径向运动，一部分材料流向齿顶外侧；齿廓B、C侧附近的材料沿其轮廓线所指向的齿顶方向流动。再次，全面分析了影响精冲齿顶塌角大小的各种因素，找出压边力和反顶力对塌角大小的影响规律，得出反顶力比压边力对控制塌角的效果更显著。最后，提出了在齿形零件精冲成形过程中减小或消除齿顶塌角的具体措施对策。

For the problem of the tooth crown collapse angle in fine blanking of tooth parts，firstly, the geometric characteristics of tooth parts and characteristics of fine blanking were analyzed, and the relationship between these features and the collapse angle of tooth parts during fine blanking was also analyzed. Then, the deformation zone of fine blanking was divided into two core deformation zones and two deformation influencing zones, and the forming process of collapse angle in the core deformation zoneⅠwas analyzed. Furthermore, the flow law of material at the top of tooth during the forming process was found by the finite element simulation software Deform-3D. The results show that the material near the A surface at the top of tooth moves toward the top of tooth in a radial direction, and a part of material flows to the outside of the addendum. However, the material near the B and C sides flows along the contour line toward the top of tooth. Therefore, a variety of factors affecting the size of tooth crown collapse angle during fine blanking were analyzed again, and the influences of blank holder force and ejection force on the collapse angle were found out. So it is pointed out that the effect of ejection force is more significant than that of blank holder force on controlling collapse angle. Finally, the concrete measures to reduce or eliminate the tooth crown collapse angle during the fine blanking process of tooth parts were put forward.

基金项目：

国家自然科学基金资助项目（51375521）；重庆市高校优秀成果转化项目（KJZH14107）

作者简介：匡青云（1993-），男，硕士研究生 E-mail：468929231@qq.com 通讯作者：邓明（1960-），男，硕士，教授 E-mail：dm@cqut.edu.cn

参考文献：

[1]吕琳，马一龙，刘潞周，等.闭挤式精冲直齿轮时塌角的形成与控制[J]. 锻压技术，2015，40（3）：32-35.

Lyu L，Ma Y L，Liu L Z，et al. Forming and control of collapse angle for the closed-extruding fine-blanking spur gear [J]. Forging & Stamping Technology，2015，40（3）：32-35.

[2]毛华杰，蒋厚生，刘艳雄，等.斜齿圆柱齿轮旋转精冲过程模具磨损模拟分析[J]. 锻压技术，2016，41（3）：88-93.

Mao H J，Jiang H S，Liu Y X，et al. Simulation analysis on die wear in rotational fine blanking for helical gears [J]. Forging & Stamping Technology，2016，41（3）：88-93.

[3]郝高明.齿形件精冲塌角形成机理及控制工艺研究[D].北京：机械科学研究总院，2014.

Hao G M. Research on Formation Mechanism and Control Technology of Die-roll of Toothed Part in Fine-blanking Process[D].Beijing：China Academy of Machinery Science and Technology，2014.

[4]邓明，刘潞周，吕琳，等.闭挤式精冲直齿轮的材料流动分析[J].锻压技术，2014,39（6）:114-117.

Deng M，Liu L Z, Lyu L，et al. Material flow analysis of closed extrusion fine blanking spur gear[J].Forging ＆ Stamping Technology，2014, 39（6）:114-117.

[5]毛秀，张祥林，查想，等.厚板齿形零件精冲成形数值模拟与缺陷分析[J].模具工业，2014，38(2):13-16.

Mao X，Zhang X L，Zha X, et al. Numerical simulation and defect analysis of fine blanking forming for thick plate tooth profile part [J]. Die & Mould Industry，2014，38(2):13-16.

[6]吕琳，刘亚琦，刘潞周，等.闭挤式精冲成形直齿轮的齿顶撕裂问题[J]. 锻压技术，2015，40（4）：20-23.

Lyu L，Liu Y Q，Liu L Z，et al. Tooth top tearing problem of closed extruding fine blanking forming for spur gear [J]. Forging & Stamping Technology，2015，40（4）：20-23.

[7]夏琴香，胡玄通，陈登，等.精冲技术的研究现状与发展趋势[J]. 锻压技术，2015，40（7）：1-6.

Xia Q X，Hu X T，Chen D，et al. Current research and development tendency of fine blanking technology [J]. Forging & Stamping Technology，2015，40（7）：1-6.

[8]张缓缓，董吉洪，李威.50钢精冲剪切面磨料磨损性能的实验研究[J]. 锻压技术，2015，40（7）：107-112.

Zhang H H，Dong J H，Li W. Experimental research on wear resistance of fine blanking shearing surface for 50 steel [J]. Forging & Stamping Technology，2015，40（7）：107-112.

[9]武汉理工大学.一种减小或消除塌角的精冲成形方法[P].中国：CN 105921598，2016-03-02.

Wuhan University of Technology. Fine blanking forming method for reducing or eliminating angle of collapse[P].China：CN 105921598，2016-03-02.

[10]钟剑波.无塌角精冲技术及其应用 [J].锻造与冲压,2016，（8）:19-21.

Zhong J B. Fine blanking technology without collapse angle and its application[J].Forging and Stamping, 2016，（8）:19-21.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】