齿板精冲时的齿顶开裂分析及控制策略

英文标题：Analysis and control strategies on tooth top cracking during fine blanking

作者：吕琳匡青云汪义高邓明

分类号：TG381

出版年,卷(期):页码：2018,43(11):17-23

摘要：

针对精冲成形齿形零件齿顶开裂这一缺陷，以理论分析、数值模拟和物理实验相结合的方法，对齿形零件精冲成形齿顶开裂形成原因进行分析，指出成形过程中齿顶开裂的形成原因是由于成形过程中齿顶所受摩擦力较大，导致齿顶变形区产生较大的拉应力并达到一定数值所致。开裂发生的时机是成形过程进行至整个精冲过程的60%~80%时。分析了齿顶开裂的主要影响因素和主要工艺参数润滑、压边力、反顶力对齿顶开裂的影响规律，并进行了实验验证。指出润滑条件对齿形零件成形质量影响最大，提出了防止齿顶开裂的策略。

For the tooth top cracking during the fine blanking process of tooth part, the causes of the tooth top cracking in the fine blanking of tooth part were analyzed based on the combination of theoretical analysis, numerical simulation and physical experiment. Then, it was pointed out that the cause of the tooth top cracking in the forming process was due to the larger friction force on the tooth top in the forming process, which caused the larger tensile stress in the deformation zone of the tooth top to reach a certain value, and the time for cracking was 60%-80% of the whole fine blanking process. Furthermore, the influences of the main influence factors and technological parameters such as lubrication, blank holder force and counterforce on the tooth top cracking were analyzed, and verified by the experiment. Finally, it is pointed out that the lubrication condition has the greatest influence on the forming quality of tooth parts. And the strategies of preventing the tooth top cracking were put forward.

基金项目：

国家自然科学基金资助项目（51375521）;重庆市高校优秀成果转化项目（KJZH14107）

作者简介：吕琳（1968-），女，硕士，教授,E-mail：lulin@cqut.edunom;通讯作者：邓明（1960-），男，硕士，教授,E-mail：dm@cqut.edu.cn

参考文献：

[1]毛秀, 张祥林, 查想, 等. 厚板齿形零件精冲成形数值模拟与缺陷分析[J]. 模具工业, 2014, (2):13-16.

Mao X, Zhang X L, Zha X, et al. Numerical simulation and defect analysis of fine blanking forming for thick plate tooth profile part [J]. Die & Mould Industry，2014, (2):13-16.

[2]邓明, 王若璜. 精密轮廓件的精冲技术现状及发展趋势[J]. 锻压技术, 2015, 40(11): 1-7.

Deng M，Wang R H. Current situation and development tendency of fine blanking technology for precise contour parts[J]. Forging & Stamping Technology, 2015, 40(11): 1-7.

[3]匡青云，吕琳，邓明，等. 齿形件精冲成形时的齿顶塌角分析及措施[J]. 锻压技术, 2017, 42(11): 26-32.

Kuang Q Y, Lyu L, Deng M，et al. Analysis and measure on tooth crown collapse angle in fine blanking for tooth parts[J]. Forging & Stamping Technology, 2017, 42(11): 26-32.

[4]韩济才, 周杰, 吕琳, 等. 精冲摩擦片齿部变形区的显微力学行为分析[J]. 塑性工程学报, 2017, 24 (5): 113-116, 124.

Han J C, Zhou J, Lyu L, et al. Analysis of the micro mechanical behavior of tooth deformation zone in fine blanking friction plate [J]．Journal of Plasticity Engineering, 2017, 24 (5): 113-116, 124.

[5]吕琳, 刘亚琦, 刘潞周, 等. 闭挤式精冲成形直齿轮的齿顶撕裂问题[J]. 锻压技术, 2015, 40(4): 20-23.

Lyu L, Liu Y Q, Liu L Z, et al. Tooth top tearing problem of closed extruding fine blanking forming for spur gear [J]. Forging & Stamping Technology, 2015, 40(4): 20-23.

[6]吕琳, 马一龙, 刘潞周, 等. 闭挤式精冲直齿轮时塌角的形成与控制[J]. 锻压技术, 2015, 40(30): 32-35.

Lyu L, Ma Y L, Liu L Z, et al. Forming and control of collapse angle for the closed-extruding fine-blanking spur gear [J]. Forging & Stamping Technology, 2015, 40(30): 32-35.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】