基于DB.12Cr2Mo1V钢的大型四辊卷板机卷板减薄分析

英文标题：Thinning analysis on large four-roll plate rolling machine based on DB.12Cr2Mo1V steel

作者：高淑娟

单位：淄博职业学院

分类号：TG335

出版年,卷(期):页码：2019,44(12):33-39

摘要：

通过有限元分析仿真模拟软件Simufact建立板材卷制模型，开展了基于DB.12Cr2Mo1V钢的卷板成形工艺模拟设计，找出板材成形后最大减薄量出现的位置并与实际生产中测量的板材厚度减薄量进行对比，以掌握板材塑性成形技术中的减薄机理，形成有效的缺陷控制方法。有限元分析结果表明：板材成形过程中的等效塑性应变的最大值出现在板材边缘处，由第3道次中左侧辊对板材成形的过度挤压所导致，并观测到板材的中性层发生内移；板材成形过程中最大减薄量出现在板材前端预弯处，减薄量为2.2 mm，与实际生产中测得的结果吻合度较高。最后，提出针对性的优化方案，对实际生产具有一定的参考价值。

A sheet rolling model was built by finite element analysis simulation software Simufact, and the simulation design of the rolling process for DB.12Cr2Mo1V steel was developed. Then, the position where the maximum thinning amount of sheet occured was found and compared with the measured amount in the actual production in order to grasp the thinning mechanism in the plastic forming technology of sheet metal and form an effective control method of defects. The results of finite element analysis show that the maximum value of equivalent plastic strain in the sheet forming process occurs at the edge of sheet, which is caused by the excessive extrusion of sheet by the left side roller in the third pass, and the neutrality layer of sheet is moved inward. Furthermore, the maximum thinning amount in the sheet forming process occurs at the front end of sheet, and the thinning amount is 2.2 mm, which is in good agreement with the measured results in the actual production. Finally, a targeted optimization scheme is proposed, which has certain reference value for the actual production.

基金项目：

高淑娟（1980-）女，硕士，讲师 E-mail：937645205@qq.com

参考文献：

［1］邢伟荣.卷板机的现状与发展
［J］.锻压装备与制造技术,2010,45(2):10-16.

Xing W R. Status and development of the bending machine for plate
［J］. China Metalforming Equipment & Manufacturing Technology,2010,45(2):10-16.

［2］严志远.水平下调式三辊卷板机工艺研究与结构分析
［D］. 太原：太原科技大学,2011.

Yan Z Y. Study on the Technology of and Analyze the Structure of the Horizontal and Downregulated Three-roller Plate Rolle
［D］. Taiyuan: Taiyuan University of Science and Technology,2011.

［3］岳明英.四辊卷板机卷板过程的分析
［D］.兰州: 兰州交通大学，2014.

Yue M Y. Analysis for the Plate Bending Process of the Four-roll Plate Bending Machine
［D］. Lanzhou: Lanzhou Jiaotong University, 2014.

［4］赵德金.基于虚拟制造的金属板材成形加工仿真技术研究
［D］. 南京: 南京理工大学，2012.

Zhao D J. Research on Simulation Technology of Sheet Metal Forming Based on Virtual Manufacturing
［D］. Nanjing: Nanjing University of Science and Technology,2012.

［5］朱传敏, 王凯. 中厚板弯曲过程中板厚变化的研究及数值模拟
［J］. 中国工程机械学报, 2013, 11(6):494-497.

Zhu C M, Wang K. Numerical simulation on thickness variations of medium-thickness plates during bending process
［J］. Chinese Journal of Construction Machinery, 2013, 11(6):494-497.

［6］孙树亮,侯英玮.中厚板塑性弯曲减薄计算及试验研究
［J］.塑性工程学报,2010,17(4):13-15.

Sun S L, Hou Y W. Calculation and experimental research on thinning during plate bending
［J］. Journal of Plastic Engineering, 2010, 17(4): 13-15.

［7］翟福宝,林新波,张质良,等.有限元模拟在金属塑性成形中的应用
［J］.锻压机械,2000,26(5):98-101.

Di F B, Lin X B, Zhang Z L, et al. Application of FE simulation in metal forming
［J］. Metalforming Machinery, 2000, 26(5): 98-101.

［8］侯英玮, 吴倩. 基于DEFORM软件的中厚板弯曲减薄规律
［J］. 大连交通大学学报, 2011, 32(3):53-56.

Hou Y W, Wu Q. Study of plate bend thinned law based on the DEFORM software
［J］. Journal of Dalian Jiaotong University, 2011, 32(3): 53-56.

［9］贺广零,罗文波,卢晋福,等.宽板弯曲成形过程中的板厚变化规律
［J］. 塑性工程学报, 2006, 13(6): 48-51.

He G L, Luo W B, Lu J F, et al. Thickness variation of wide sheet in bending forming
［J］. Journal of Plasticity Engineering, 2006, 13(6): 48-51.

［10］罗锐, 程晓农, 徐桂芳,等. 新型Fe-20Cr-30Ni-0.6Nb-2Al-Mo合金的热变形行为及本构模型
［J］. 稀有金属, 2017,41(2):132-139.

Luo R, Cheng X N, Xu G F, et al. Constitutive modeling for elevated temperature flow behavior of Fe-20Cr-30Ni-0.6Nb-2Al-Mo alloy
［J］. Chinese Journal of Rare Metals, 2017,41(2):132-139.

［11］张度宝, 汪涛, 鱼银虎,等. Ni-Al含能结构材料冲击释能行为研究
［J］. 稀有金属, 2017,41(1): 40-44.

Zhang D B, Wang T, Yu Y H, et al. Impact energy release behaviors of Ni-Al energetic structural material
［J］. Chinese Journal of Rare Metals, 2017,41(1): 40-44.

［12］栾小东, 魏会莎, 岳玉梅. 厚板弯曲成形有限元数值模拟及工艺研究
［J］. 热加工工艺, 2014,43(21):142-144,148.

Luan X D, Wei H S, Yue Y M. FE simulation and process research on plate bending forming
［J］. Hot Working Technology, 2014,43(21):142-144,148.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】