微量元素碳对GH4169合金性能的影响

英文标题：Influence of trace element carbon on properties for GH4169 alloy

分类号：TG132.3

出版年,卷(期):页码：2019,44(12):153-158

摘要：

采用JMatPro V7.0软件对不同碳含量的GH4169合金性能进行计算，研究微量元素碳对GH4169合金力学性能及蠕变性能的影响。结果表明：碳含量对γ″相含量有显著影响，随着碳元素含量的增加，γ″相含量先降低至碳含量为0.01%处再上升，当碳含量为0.02%时，γ″相含量开始降低至碳含量为0.05%处再上升；随碳元素含量的增加，室温屈服强度先减小至碳含量为0.01%处后增加，当碳含量为0.02%时，室温屈服强度开始降低后上升，在碳含量为0.05%处，出现极小值；蠕变速率的变化趋势与室温屈服强度相反，随碳含量的增加，蠕变速率在碳含量小于0.02%时先增大再减小，当碳含量高于0.02%时，仍然呈先增大后减小的趋势，极大值出现于碳含量为0.05%处，此时持久寿命较短，蠕变性能不佳；杨氏模量随着碳含量的增加呈现上升趋势。

The properties of GH4169 alloy with different carbon contents were calculated by software JMatPro V7.0, and the influences of trace element carbon on mechanical and creep properties of GH4169 alloy were investigated. The results show that the carbon content has significant influence on the amount of γ″ phase, and with the increasing of carbon content, the content of γ″ phase decreases firstly until the carbon content reaches 0.01% and then increases. When the carbon content is up to 0.02%, the content of γ″ phase decreases again until the carbon content reaches 0.05% and then increases, and with the increasing of carbon content, the yield strength at room temperature decreases firstly until the carbon content reaches 0.01% and then increase. When the carbon content is up to 0.02%, the yield strength at room temperature decreases again and then increases, the minimum value exists when the carbon content reaches 0.05%. However, the trend of creep rates is contrary to that of the yield strength at room temperature, and with the increasing of carbon content, the creep rate increases firstly and then decreases when the carbon content is less than 0.02%. When the carbon content is more than 0.02%, the creep rate increases firstly and then decreases continually, and the maximum value occurs when the carbon content reaches 0.05%. Meanwhile, the creep rupture life is short, the creep property is not good, and the Young′s modulus increases with the increasing of carbon content.

基金项目：

中央高校基本科研业务费专项资金项目（3102019 ZX004）

袁颖菁（1997-），女，硕士研究生 E-mail：yuanyingjing@foxmail.com 通讯作者：王建国（1987-），男，博士，助理研究员 E-mail:wjgnll@126.com

参考文献：

［1］庄景云,杜金辉,邓群,等. 变形高温合金GH4169
［M］.北京：冶金工业出版社,2006.

Zhuang J Y,Du J H,Deng Q,et al. Wrought Superalloy GH4169
［M］. Beijing:Metallurgical Industry Press,2006.

［2］郭建亭. 高温合金材料学
［M］. 北京: 科学出版社,2008.

Guo J T. Materials Science and Engineering for Superalloys
［M］. Beijing:Science Press,2008.

［3］都贝宁,盛立远,赖琛,等.一种镍基高温合金蠕变过程中碳、硼化物的演变行为及结构表征
［J］.稀有金属材料与工程,2017,46(8):2123-2129.

Du B N,Sheng L Y,Lai C,et al. Evolution and structure characterization of carbide and boride during creep in a Ni-based superalloy
［J］. Rare Metal Materials and Engineering,2017,46(8):2123-2129.

［4］张鹏,杨凯,朱强,等.微量元素对镍基高温合金微观组织与力学性能的影响
［J］.精密成形工程,2018,10(2):1-6.

Zhang P,Yang K,Zhu Q,et al. Effect of microelement on microstructure and mechanical property of nickel-base superalloy
［J］. Journal of Netshape Forming Engineering,2018,10(2):1-6.

［5］余乾.微量元素C和Mg对一种镍基高温合金组织和力学性能的影响
［J］.航空材料学报,2006，(4):11-13.

Yu Q. Influences of C and Mg on microstrcutures and mechanical properties of a nickel base superalloy
［J］. Journal of Aeronautical Materials,2006，(4):11-13.

［6］孙新涛. 碳在一种镍基单晶高温合金中的作用
［D］.沈阳：沈阳工业大学,2007.

Sun X T. The Effect of Carbon on a Nickel Base Single Crystal Superalloy
［D］. Shenyang:Shenyang University of Technology,2007.

［7］王兴,邓家彬,王瑞琴,等.钛合金薄板轧制工艺对加工硬化指数的影响
［J］.热加工工艺,2015,44(17):128-129，133.

Wang X,Deng J B,Wang R Q,et al. Effects of working hardening exponent on rolling process of titanium alloy sheet
［J］. Hot Working Technology,2015,44(17):128-129，133.

［8］姚利丽,底华芳,王威,等.珠光体钢丝冷变形加工硬化行为研究
［J］.热加工工艺,2017,46(1):69-73.

Yao L L,Di H F,Wang W,et al. Study on work hardening behavior of cold deformation of pearlite steel wires
［J］. Hot Working Technology,2017,46(1):69-73.

［9］陈国良. 高温合金学
［M］. 北京: 冶金工业出版社,1988.

Chen G L. Superalloys
［M］. Beijing:Metallurgical Industry Press,1988.

［10］吕钟,周健,孙志梅,等.稀土元素对镁合金结构及力学性能的影响
［J］.科学通报,2013,58(1):98-102.

Lyu Z,Zhou J,Sun Z M,et al. The effect of rare earth element on microstructure and mechanical properties of magnesium alloys
［J］. Chinese Science Bulletin,2013,58(1):98-102.

［11］田素贵,赵忠刚,陈礼清,等. 直接时效处理对热连轧GH4169合金蠕变行为的影响
［J］.航空材料学报,2010,30(5):14-18.

Tian X G,Zhao Z G,Chen L Q,et al. Influence of direct aged treatment on creep behaviors of hot continuous rolling GH4169 superalloy
［J］. Journal of Aeronautical Materials,2010,30(5):14-18.

［12］刘臣,田素贵,王欣,等. 一种GH4169镍基合金的组织结构与蠕变性能
［J］.材料工程,2017,45(6):43-48.

Liu C,Tian X G,Wang X,et al. Microstructure and creep property of a GH4169 nickel-based superalloy
［J］. Journal of Materials Engineering,2017,45(6): 43-48.

［13］余宸旭,肖来荣,赵小军,等.C元素的添加对Nb-20Ti-16Al合金组织和性能的影响
［J］.稀有金属,2017,41(9):980-984.

Yu C X,Xiao L R,Zhao X J,et al. Microstructure and mechanical properties of Nb-20Ti-16Al alloy with carbon addition
［J］. Chinese Journal of Rare Metals,2017,41(9):980-984.

［14］张熹雯,胡海涛,朱春雷,等.微量C对层片组织TiAl合金高应力蠕变变形的影响
［J］.稀有金属,2017,41(9):972-979.

Zhang X W,Hu H T,Zhu C L,et al. Deformation behavior during creep of lamellar TiAl alloys at relatively high stress with minor C alloying addition
［J］. Chinese Journal of Rare Metals,2017,41(9):972-979.

服务与反馈：

【文章下载】【加入收藏】