GH4169合金小余量小尺寸静子叶片锻造工艺及显微组织控制

英文标题：Forging process and microstructure control for alloy GH4169 stator blade with little allowance and small size

作者：黄明星汪大成罗希孙敏

关键词：GH4169合金叶片小余量锻造显微组织

分类号：TG316.3

出版年,卷(期):页码：2020,45(1):41-46

摘要：

针对GH4169合金叶片锻件粗晶、混晶等晶粒组织不合格问题，以某压气机小余量小尺寸静子叶片锻件为研究对象，首先分析锻件结构，确定锻造工艺路线，然后通过选取2种规格坯料、5个变形量、4个锻造温度来组成12组试验，探究变形量、锻造温度对组织的影响以及演化规律，同时对选取的保温时间、锻造火次的稳定性进行分析，得到合理锻造工艺参数。研究表明，变形量在35%～45%内可获得均匀的组织，但对晶粒度大小无明显影响；温度是影响晶粒度的主要因素，大于1000 ℃时叶身晶粒粗化现象明显，在990~1000 ℃之间叶身可获得细腻、均匀的组织；预锻时组织已成形稳定，终锻无明显变化，在选取的保温时间内组织稳定；在变形量40%及锻造温度990 ℃下获得的叶片锻件具有优良的综合力学性能及细晶组织，均高于标准要求。

For the unqualified problem of grain structure for alloy GH4169 blade forgings, such as mixed grains and coarse grains, based on stator blade of a compressor with little allowance and small size, the forging process route was determined by analysis of forging structure, and the influences and evolution laws of deformation and forging temperature on microstructures were analyzed by twelve sets of experiments consisting of two kinds of billets, five different deformation amounts and four different forging temperatures. Meanwhile, the stability of selected holding time and forging times was analyzed, and the reasonable forging process parameters were obtained. The results show that the deformation amount of 35%-45% obtains uniform structure,but has less effect on grain size. The temperature is the major factor affecting on grain size. However, the grain growth of blade body is obvious when the temperature is over 1000 ℃, and the fine grain of blade body is obtained when the temperature is 990-1000 ℃. Furthermore, the structure is stable during pre-forging, and there is no obvious change in final forging, which means the grain structure is stable in the selected holding time. Thus, the superior comprehensive mechanical properties and fine grain structure of blade forgings are obtained with the deformation amount of 40% and the forging temperature of 990 ℃, which are higher than standard requirements.

基金项目：

企业研发项目（KT16Y018-YIY）

作者简介：黄明星(1987-)，男，硕士，工程师 E-mail：78970650@qq.com

参考文献：

[1]张志文.叶片锻造[M].西安:西安交通大学出版社, 1987.

Zhang Z W. Blade Forging[M].Xi′an: Xi′an Jiaotong University Press, 1987.

[2]袁兆静,刘劲松,张士宏.GH4169合金δ相的析出动力学研究[J].沈阳理工大学学报,2010,29(2):23-26.

Yuan Z J, Liu J S, Zhang S H. Research on precipitation kinetics of δ-phase in GH4169 alloy [J]. Journal of Shenyang Ligong University, 2010,29(2):23-26.

[3]余江山.高温合金叶片精锻成形研究[Ｄ].沈阳：沈阳理工大学，2008.

Yu J S. Research on Precision Forging of High Temperature Alloy Blade [D]. Shenyang: Shenyang Ligong University, 2008.

[4]庄景云，杜金辉，邓群.GH4169合金及锻件晶粒形貌特点[J].钢铁研究学报，2003, 15(7): 44-48.

Zhuang J Y，Du J H，Deng Q. Grain morphologies characteristics of alloy GH4169 and forgings[J].Journal of Iron and Steel Research, 2003, 15(7): 44-48.

[5]叶璋，高玉魁.基于DEFORM-2D的GH4169合金涡轮盘的热模锻残余应力研究[J]. 锻压技术,2018, 43(3):1-7.

Ye Z, Gao Y K. Study on residual stress of hot die forging for alloy GH4169 turbine disc based on DEFORM-2D[J]. Forging & Stamping Technology, 2018, 43(3):1-7.

[6]张翔，王高潮，甘雯晴，等. GH4169合金零件的冷挤压成形工艺[J]. 锻压技术,2019, 44(4):101-105.

Zhang X, Wang G C, Gan W Q, et al. Cold extrusion forming process of GH4169 alloy parts[J]. Forging & Stamping Technology, 2019, 44(4):101-105.

[7]李淼泉，李浩放，熊爱明，等. 带阻尼台TC6钛合金叶片精密锻造[J]. 锻压技术,2018, 43(7):96-102.

Li M Q, Li H F, Xiong A M, et al. Precision forging of TC6 titanium alloy blade with damping[J]. Forging & Stamping Technology, 2018, 43(7):96-102.

[8]李艳芹，张德海，谢贵重，等. 叶片锻造有限元模拟及试验的微观组织研究[J]. 锻压技术,2018, 43(4):9-15.

Li Y Q, Zhang D H, Xie G Z, et al. Research on microstructure of finite element simulation and experiment for forging blade[J]. Forging & Stamping Technology, 2018, 43(4):9-15.

[9]邰清安，关红，国振兴，等. 一种高强GH4169合金转子叶片精密成形技术研究[J].钢铁研究学报,2011,23(S2):174-177.

Tai Q A, Guan H, Guo Z X, et al. Investigation on a precise forming technology for high-strength GH4169 rotor blade [J]. Journal of Iron and Steel Research, 2011,23(S2):174-177.

[10]GB/T 6394—2002, 金属平均晶粒度测定方法[S].

GB/T 6394—2002, Determination of estimating the everage grain size of metal[S].

[11]蔡建明,张旺峰,李臻熙,等.TC11钛合金叶片上亮条和暗条的性质及控制[J].材料工程,2005，33(1):16-19.

Cai J M, Zhang W F, Li Z X, et al. Characteristic and control of bright and dark striations in TC11 titanium alloy blades [J]. Journal of Materials Engineering, 2005, 33(1):16-19.

[12]庄景云.等变形高温合金GH4169锻造工艺[M]. 北京:冶金工业出版社, 2008.

Zhuang J Y. Forging Process of Wrought Super Alloy GH4169[M]. Beijing: Metallurgical Industry Press, 2008.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】