自冲铆接凹模损伤对铆接质量的影响

英文标题：Influence of self-piercing riveting die damage on riveting quality

作者：潘伟涛王健强亢剑梁端顾杰

单位：合肥工业大学

分类号：TG386

出版年,卷(期):页码：2020,45(1):162-167

摘要：

采用了试验结合有限元仿真的方法，对自冲铆接(Self\|Piercing Riveting,SPR）设备中的重要部件凹模出现的不同程度的损伤情况可能对SPR接头质量产生的影响进行了试验研究。对凹模的受损情况进行统计分类，根据凹模的受损程度将凹模分为早期受损、中前期受损等5个级别。使用不同受损程度的凹模对厚度为1.5 mm的A6111铝板进行自冲铆接，测量铆接接头的外观质量与接头剖面几何参数。通过拉伸-剥离仿真试验，探究凹模断裂损伤对SPR铆接接头的连接质量的影响。试验结果表明：凹模损伤会对接头表面外观质量造成损伤，并且会随着凹模损伤程度的增加而增大；凹模没有发生断裂时，凹模损伤对接头剖面的几何参数不会产生太大影响；凹模发生断裂，会降低接头的连接质量。

The influences of varying degrees for die damage in self\|piercing riveting (SPR) equipment on the quality of SPR riveted joints were studied by the method of experiment and finite element simulation. Then, the die damages were classified. And according to the die damage degrees, the die damages were divided into five levels, such as early damage and middle early damage, etc. Furthermore, A6111 aluminum sheet with thickness of 1.5 mm was riveted by damaged dies with varying degrees, and the appearance quality of riveted joints and geometric parameters of joint section were measured. The influence of die fracture damage on the joint quality of SPR riveted joint was investigated by tension peeling simulation experiment. The experimental results show that the die damages could damage the appearance quality of joint surface, and the damages increase with the increasing of the damage degree of die. When the die does not fracture, the die damages have little effect on the geometric parameters of joint section, but the fracture of die reduces the riveting quality.

基金项目：

潘伟涛（1994-），男，硕士 E-mail：18655187903@163.com

参考文献：

[1]李永兵,马运五,楼铭,等.轻量化多材料汽车车身连接技术进展[J].机械工程学报,2016,52(24):1-23.

Li Y B, Ma Y W, Lou M, et al. Advances in welding and joining processes of multi material lightweight car body[J]. Journal of Mechanical Engineering, 2016,52(24):1-23.

[2]吴志兵,杨建,吴雄伟,等.车身外造型关键区域分缝研究[J].锻压技术,2019,44(10):56-63.

Wu Z B，Yang J，Wu X W，et al. Research on key area parting for car body exterior[J]. Forging & Stamping Technology, 2019,44(10):56-63.

[3]吴小丹，王敏，孔谅，等.SPR自冲铆接技术研究现状及应用前景[J].电焊机，2016，46(4)：31-36.

Wu X D, Wang M, Kong L, et al. Research status and application prospects of SPR technology [J]. Electric Welding Machine, 2016, 46(4): 31-36.

[4]申仲达.铝合金车身自冲铆工艺与力学性能研究[D].合肥：合肥工业大学，2018.

Shen Z D. Study on Self-piercing Riveting and Mechanical Properties of Aluminum Alloy Body[D]. Hefei: Hefei University of Technology, 2018.

[5]邢保英.自冲铆连接机理及力学性能研究[D].昆明：昆明理工大学,2014.

Xing B Y. Investigation of Forming Mechanism and Mechanical Property of Self-piercing Riveted Joints[D]. Kunming: Kunming University of Science and Technology,2014.

[6]王淑俊,王双枝,刘莉,等.980QP先进高强钢的冲压成形工艺[J].锻压技术,2019,44(4):64-68.

Wang S J，Wang S Z，Liu L，et al. Stamping process of advanced 980QP high strength steel[J]. Forging & Stamping Technology, 2019,44(4):64-68.

[7]林巨广,钱让发,袁波,等. 热熔自攻丝连接工艺的分析与优化[J].组合机床与自动化加工技术,2019,(1):141-143.

Lin J G, Qian R F, Yuan B, et al. Analysis and optimization of flow drew screw technology[J]. Modular Machine Tool & Automatic Manufacturing Technique, 2019, (1):141-143.

[8]汪洋.白车身无钉铆接工艺及铆点力学性能研究[D].合肥：合肥工业大学，2017.

Wang Y. The Clinching Process and Clinching Point Mechanical Properties Research [D]. Hefei: Hefei University of Technology, 2017.

[9]唐涛,李志强,门向南,等.航空大型复杂蒙皮的拉伸成形技术[J].锻压技术,2019,44(7):57-61.

Tang T，Li Z Q，Men X N，et al. Stretch forming technology of aviation large and complex skin[J]. Forging & Stamping Technology, 2019,44(7):57-61.

[10]王健强,汪洋,荣海龙,等.影响无钉铆接质量的工艺参数权重研究[J].合肥工业大学学报:自然科学版,2017,40(1):1-6.

Wang J Q, Wang Y, Rong H L, et al. Study of weights for process parameters influencing clinching joint quality[J]. Journal of Hefei University of Techenology: Natural Science, 2017, 40(1): 1-6.

[11]韩金娥. 汽车铝合金前盖滚边工艺仿真研究及实验验证[D]. 合肥：合肥工业大学,2017.

Han J E . The Simulation Analysis and Experimental Study of Roller Hemming Process on Aluminum Alloy Hood[D]. Hefei: Hefei University of Technology, 2017.

[12]Zeng L, Xia Y, Zhao H, et al. On utilization of material failure criterion in modeling pull out failure of spot welded joints [A]. ASME 2013 International Mechanical Engineering Congress and Exposition, American Society of Mechanical Engineers Digital Collection[C]. American, 2013.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】