大尺寸弹丸喷丸成形7B50铝合金材料的变形规律

英文标题：Deformation law of 7B50 aluminum alloy in shot peening for large size projectiles

作者：时圣革王明涛白雪飘陈福龙

单位：1.海装驻北京地区第五军事代表室 2.中国航空制造技术研究院 3.塑性成形技术航空科技重点试验室 4.数字化塑性成形技术及装备北京市重点试验室

分类号：V261.2

出版年,卷(期):页码：2021,46(3):96-100

摘要：

大尺寸弹丸喷丸成形是一种针对大型整体壁板塑性成形的有效手段。采用正交试验方法对7B50铝合金平板试件开展大尺寸弹丸喷丸成形工艺试验，研究不同工艺参数下喷丸后试件沿弦向和展向曲率半径的变化规律。结果表明：试件在喷丸成形后呈球面凸起变形，且沿弦向的曲率半径小于沿展向的曲率半径；各因素按对曲率半径的影响程度排序依次为喷丸气压>试件厚度>移动速度；曲率半径随着厚度和移动速度的增加而增加，随着喷丸气压的增加而减小；建立了可以反映曲率半径与3个因素之间定量关系的回归方程，可为今后喷丸成形的变形预测提供参考。

Shot peening with large size projectiles is an effective plastic forming method for integral panels. Therefore, for 7B50 aluminum alloy plate specimens, the experiments of shot peening process with large size projectiles were conducted by orthogonal experiment, and the changing rules of curvature radius along the chord and span directions of specimens after shot peening under different process parameters were studied. The results show that after shot peening, the specimen is deformed into a spherical convex, and the curvature radius along the chord direction is smaller than that along the span direction. The influence order of various factors on the curvature radius is pressure of shot peening>specimen thickness>moving speed. Besides, the curvature radius increases with the increasing of specimen thickness and moving speed and decreases with the increasing of pressure of shot peening. Thus, the regression equation that can reflect the quantitative relationships between the curvature radius and the three factors is established, which provides the basic reference for predicting deformation of shot peening.

基金项目：

时圣革（1973-），男，硕士，高级工程师 E-mail：15910627299@139.com 通讯作者：王明涛（1986-），男，硕士，高级工程师 E-mail：5iwangming@163.com

参考文献：

[1]曾元松.航空钣金成形技术[M].北京:航空工业出版社, 2014.

Zeng Y S.Aviation Sheet Metal Forming Technology [M].Beijing: Aviation Industry Press, 2014.

[2]Shang J Q, Zeng Y S.Shot forming technology and its development trend and thinking[J].Aeronautical Manufacturing Technology, 2010, 16: 26-29.

[3]Kulkarni K M, Schey J A, Badger D V.Investigation of shot peening as a forming process for aircraft wing skins[J].Journal of Applied Metalworking, 1981,1(4):34-44.

[4]Yamada T，Takahashi T，Ikeda M，et al.Development of shot peening for wing integral skin for continental business jets[J].Technical Review,2002,39(2): 57-61.

[5]Bai X P, Zeng Y S, Meng Q，et al.Experimental investigation on shot peen forming of 2198 Al-Li alloy plate[A].12th International Conference on Shot Peening[C].Goslar, Shotpeener, 2014.

[6]Zeng Y, Huang X.Forming technology of large integral panel[J].Acta Aeronautica Et Astronautica Sinica, 2008, 29(3):721-727.

[7]Kopp R, Schulz J.Flexible sheet forming technology by double-sided simultaneous shot peen forming[J].CIRP Annals-Manufacturing Technology, 2002，51(1):195-198.

[8]Frises A.KSA develops new automated peen forming for wing skins[J].The Shot Peener, 2006,20(4): 16-17.

[9]Miao H Y, Demers D, Larose S, et al.Experimental study of shot peening and stress peen forming[J].Journal of Materials Processing Technology, 2010, 210(15):2089-2102.

[10]Gariépy A, Larose S, Perron C, et al.On the effect of the orientation of sheet rolling direction in shot peen forming[J].Journal of Materials Processing Technology, 2013, 213(6):926-938.

[11]Russig C, Bambach M, Hirt G, et al.Shot peen forming of fiber metal laminates on the example of GLARE[J].International Journal of Material Forming, 2014, 7(4):425-438.

[12]高国强, 王永军, 张万瑜,等.喷丸成形工艺参数对成形曲率半径的影响分析[J].锻压技术，2014, 39（9）：53-57.

Gao G Q, Wang Y J, Zhang W Y, et al.Influence analysis of shot peening forming technological parameters on formed curvature radius[J].Forging & Stamping Technology, 2014, 39（9）：53-57.

服务与反馈：

【文章下载】【加入收藏】