成形温度对铝合金型材挤压-弯曲一体化成形回弹及 截面畸变的影响
英文标题:Influence of forming temperature on springback and cross-section distortion for aluminum alloy profile during extrusion-bending integration forming
作者:许亮 徐从昌 李落星 
单位:湖南大学 机械与运载工程学院 
关键词:铝型材 挤压-弯曲一体化成形 回弹 截面畸变 尺寸精度 
分类号:TG376
出版年,卷(期):页码:2021,46(9):154-162
摘要:

 采用实验与仿真相结合的方法,研究了成形温度对挤压-弯曲一体化成形铝合金方管型材的回弹和截面畸变的影响规律及机理,并与冷拉弯工艺进行了对比分析。结果表明:影响回弹量的主要因素是材料屈服强度与弹性模量的比值,该比值越高,型材的回弹量越大,反之则越小;挤压-弯曲时,材料挤出模口后仍处于温热状态,该比值较低,回弹量比T4态、T6态冷拉弯型材减小约50%75%。截面畸变由外侧拉应力主导,外侧材料的流动不均匀引起型材截面的变形,而型材内侧表面在弯曲模刚性支撑下的变形相对较小;在挤压-弯曲一体化成形工艺中,材料在高温状态下的均匀变形能力好,在0.15 kN的牵引力下,其中心位置处的截面畸变量相较于T4T6态分别减小约85%77%

 The influence laws and mechanism of forming temperature on springback and cross-section distortion of 6063 aluminum alloy square tube profile formed by extrusion-bending integration forming process and mechanism were explored by the method combining with experiment and simulation, and the comparative analysis were conducted by comparing with cold stretch-bending process. The results show that the main factor affecting the springback is the ratio of yield strength to elastic modulus, the greater the ratio of yield strength to elastic modulus, the greater the springback of the profile, and vice versa. In the extrusion-bending process, the material is still in a warm state after extruded from the mold, the ratio of the yield strength to the elastic modulus is low, the springback of the extrusion-bending profile is about 50% and 75% less than that of the cold stretch-bending profile of T4 state and T6 state respectively. In addition, the cross-sectional distortion is dominated by the external tensile stress, the uneven flow of the external material causes the cross-section distortion of the profile, while the deformation of the inner surface of the profile under the rigid support of the bending mold is relatively small. In the extrusion-bending integrated forming process, the uniform deformation ability of the material at high temperature is good, and with a traction force of 0.15 kN, the cross-section distortion at the center position of the profile is reduced by about 85% and 77% respectively compared with that of T4 state and T6 state.

 

基金项目:
国家自然科学基金资助项目(U20A20275)
作者简介:
:许亮(1990-),男,博士研究生 E-mail:xuliang9010@126.com 通信作者:徐从昌(1989-),男,博士,助理研究员 E-mail:xuccae86@126.com
参考文献:

 [1]刁可山, 周贤宾, 金朝海. 铝合金型材拉弯成形研究进展 [J]. 塑性工程学报, 2003,10(6):38-42.


 


Diao K S, Zhou X B, Jin C H. The study on stretchbending process for aluminium extrusions [J]. Journal of Plasticity Engineering, 2003,10(6):38-42.


 


[2]徐义, 李落星, 李光耀, . 型材弯曲工艺的现状及发展前景 [J]. 塑性工程学报, 2008, 15(3):61-70.


 


Xu Y, Li L X, Li G Y, et al. Extrusion bending: method application and recent development [J]. Journal of Plasticity Engineering, 2008,15(3):61-70.


 


[3]卢立伟,盛坤,伍贤鹏,等. 镁合金挤压变形工艺的研究进展[J]. 锻压技术,2019,44(1):1-9.


 


X Lu L WSheng KWu X Pet al. Research progress of extrusion process for magnesium alloy [J]. Forging & Stamping Technology2019, 44(1):1-9.


 


 


[4]朱莉, 马泽恩, 王仲奇. 压弯成形中回弹问题的研究 [J]. 锻压装备与制造技术, 2002,37(4):31-33.


 


Zhu L, Ma Z E, Wang Z Q. Study on the resilience of bending under pressure process [J]. China Metalforming Equipment and Manufacturing Technology, 2002,37(4):31-33.


 


[5]吴建军, 张贺刚, 王俊彪, . 型材拉弯的力学与回弹分析 [J]. 材料科学与工艺, 2004, 12(4):357-359.


 


Wu J J, Zhang H G, Wang J B, et al. Mechanical and springback analysis for the stretchbending process of extruded profile [J]. Materials Science and Technology, 2004, 12 (4): 357-359.


 


[6]闵范磊, 朱光明, 常征, . 方管铝型材自弯曲挤压工艺 [J]. 中国有色金属学报, 2020, 309):2032-2040.


 


Fan F L, Zhu G M, Chang Z, et al. Selfbending extrusion process for square tube aluminum profiles [J]. The Chinese Journal of Nonferrous Metals, 2020, 309):2032-2040.


 


[7]Zhou W B, Lin J G, Dean T A, et al. Analysis and modelling of a novel process for extruding curved metal alloy profiles [J]. International Journal of Mechanical Sciences, 2018, 138-139: 524-536.


 


[8]Zhou W B, Yu J Q, Lin J G, et al. Effects of die land length and geometry on curvature and effective strain of profiles produced by a novel sideways extrusion process [J]. Journal of Materials Processing Technology, 2020, 28211):66-82.


 


[9]Müller K B. Bending of extruded profiles during extrusion process [J]. International Journal of Machine Tools & Manufacture, 2006, 46(11):1238-1242.


 


[10]李落星, 刘志文, 徐从昌, 机器人主动牵引的三维变曲率型材在线弯曲成形装置 [P]. 中国: CN107234443A, 2017-10-10.


 


Li L X, Liu Z W, Xu C C. Online bending forming device of threedimensional variable curvature profile driven by robot [P]. China: CN107234443A, 2017-10-10.


 


[11]李世康, 李落星, 刘志文, . 挤压速度对6063 铝合金管材焊合强度的影响 [J]. 中国有色金属学报, 2017, 27(9):1775-1784.


 


Li S K, Li L X, Liu Z W, et al. Effect of extrusion speed on weld strength of 6063 square tube [J]. The Chinese Journal of Nonferrous Metals, 2017, 27(9):1775-1784.


 


[12]FereshtehSaniee F, Pillinger I, Hartley P. Friction modelling for the physical simulation of the bulk metal forming processes [J]. Journal of Materials Processing Technology, 2004, 153-154:151-156.


 


[13]郭振华, 裴久杨, 樊志新, . 外方内圆铜管连续挤压数值模拟与实验研究[J]. 稀有金属, 2019, 43(1):38-43.


 


Guo Z H, Pei J Y, Fan Z X, et al. FEM simulation and experimental study on continuous extrusion process for copper tube with outer square and inner circle [J]. Chinese Journal of Rare Metals, 2019, 43(1):38-43.


 


 


[14]Liu T J, Wang Y J, Wu J J. Springback analysis of Z & Tsection 2196T8511 and 2099T83 AlLi alloys extrusions in displacement controlled cold stretch bending [J]. Journal of Materials Processing Technology, 2015, 225:295-309.


 


[15]刘志文, 李落星, 肖罡, . 热处理状态和工艺顺序对铝型材弯曲回弹的影响 [J]. 湖南大学学报:自然科学版, 2014, 41(7):23-29.


 


Liu Z W, Li L X, Xiao G, et al. Influence of heattreated condition and process sequences on the springback of aluminum bent profiles [J]. Journal of Hunan UniversityNatural Sciences, 2014, 41(7):23-29.


 


[16]Pornputsiri N, Kanlayasiri K. Effect of bending temperatures on the microstructure and springback of a TRIP steel sheet [J]. Defence Technology, 2020, 16(5):980-987.


 


[17]Kecman D. Bending collapse of rectangular and square section tubes [J]. International Journal of Mechanical Sciences, 1983, 25(9-10):623-636.


 


[18]Paulsen F, Welo T. An analytical model for prediction of tube ovalization in bending [A].


Brucato,Pr.V.(Ed.)The 6th International Esaform Conference on Material Forming[C]. SalernoItaly, 2003.

服务与反馈:
本网站尚未开通全文下载服务】【加入收藏
《锻压技术》编辑部版权所有

中国机械工业联合会主管 北京机电研究所有限公司 中国机械工程学会塑性工程分会主办
联系地址:北京市海淀区学清路18号 邮编:100083
电话:+86-010-82415085 传真:+86-010-62920652
E-mail: fst@263.net(稿件) dyjsjournal@163.com(广告)
京ICP备07007000号-9