八角杆螺栓冷镦卷边折叠缺陷研究及工艺优化

英文标题：Research on curling and folding defects for octagonal rod bolts in cold heading and process optimization

作者：李　旋李　蓉莫　杰刘　坚郑琼娥

分类号：TG376. 3

出版年,卷(期):页码：2023,48(1):14-22

摘要：

为了解决某车用八角杆螺栓冷镦生产过程中废品率高、模具寿命过短的问题, 借助DEFORM 对该螺栓冷镦成形过程进行模拟, 发现螺栓冷镦成形中形成的卷边折叠为关键要因。以消除卷边折叠、优化工艺方案为目标, 选取模具成形角α、缩径比ε、下压速度v、摩擦因数f 这4 个因素, 设计开展了L16(44) 正交试验, 获得了各因素对金属堆积卷边折叠的影响程度,结合影响趋势图获得了最优工艺参数组合, 即成形角为14°、缩径比为1. 1、下压速度为10 mm·s-1、摩擦因数为0. 08。采用最优工艺参数组合进行仿真, 结果表明: 卷边折叠问题得以消除, 金属流动性得到改善, 成形加载力减少了38. 6%, 模具上端口崩裂区域的等效应力降低了40. 3%。实际生产证明, 废品率由87. 0%降低至0. 1%, 模具过早损坏现象得到了解决。研究结果为类似折叠缺陷的改善提供了参考。

In order to solve the problems of high scrap rate and short die life in the cold heading production process of a vehicle octagonal rod bolt, the cold heading process of the bolt was simulated by software DEFORM, and the curling and folding formed during the cold heading of bolt were the key factors. Then, with the goal of eliminating the curling and folding and optimizing the process scheme, the four factors of die forming angle α, diameter reduction ratio ε, pressing speed v and friction coefficient f were selected, and L16 (44 ) orthogonal experiment was designed and carried out. Furthermore, the influence degree of each factor on the curling and folding of metal stacking was obtained, and combined with the influence trend diagram, the optimal combination of process parameters was obtained with the die forming angle of 14°, the diameter reduction ratio of 1. 1, the pressing speed of 10 mm·s-1 and the friction coefficient of 0. 08. The simulation results show that under the optimal process parameters combination, the curling and folding problems are eliminated, the metal fluidity is improved, the forming loading force is reduced by 38. 6%, and the equivalent stress in the collapse area of upper port for die is reduced by 40. 3%. The actual production proves that the scrap rate is reduced from 87. 0% to 0. 1%, and the premature damage of die is effectively solved. Thus, the research results provide a reference for the improvement of similar folding defects.

基金项目：

国家自然科学基金创新研究群体基金资助项目(51621004); 国家自然科学基金资助项目(52105096)

作者简介: 李　旋(1994-), 男, 硕士 E-mail: 1069945167@ qq. com 通信作者: 李　蓉(1976-), 女, 博士, 副教授 E-mail: jyylirong@ hnu. edu. cn

参考文献：

[1] 　肖志玲. 多工位高速冷镦成形机理及其设备结构优化研究[D]. 北京: 中国机械科学研究总院集团有限公司, 2015.

Xiao Z L. Research on Multi Station High Speed Cold Heading Forming Mechanism and Equipment Structure Optimization [D]. Beijing: China Academy of Machinery Science and Technology Group, 2015.

[2] 　李光耀, 王琥. 板料冲压成形工艺与模具设计制造中的若干前沿技术[J]. 机械工程学报, 2010, 46 (10): 31-39.

Li G Y, Wang H. Some advanced technologies in sheet metal stamping process and die design and manufacturing [J]. Chinese Journal of Mechanical Engineering, 2010, 46 (10): 31-39.

[3] 　李红英. 金属塑性加工模具设计与制造 [M]. 北京: 化学工业出版社, 2009.

Li H Y. Design and Manufacture of Metal Plastic Processing Die [M]. Beijing: Chemical Industry Press, 2009.

[4] 　吕炎. 锻件缺陷分析与对策[M]. 北京: 机械工业出版社,1999.

Lyu Y. Analysis and Countermeasures of Forging Defects [M].Beijing: China Machine Press, 1999.

[5] 　胡建军, 李小平. 基于Deform-3D 塑性成形CAE 应用教程[M]. 北京: 北京大学出版社, 2011.

Hu J J, Li X P. CAE Application Course Based on Deform-3D Plastic Forming [J]. Beijing: Peking University Press, 2011.

[6] 　Kim H, Altan T, Sevenler K. Computer-aided part and processingsequence design in cold forging [J]. Journal of Materials Processing

Technology, 1992, 33, (1): 57-74.

[7] 　朱宝辉, 钟景明, 汪凯, 等. 高强度铍铜合金QBe2 棒材室温旋转弯曲疲劳行为[J]. 稀有金属, 2021, 45 (10): 1153-1161.

Zhu B H, Zhong J M, Wang K. Rotational bending fatigue behavior of high strength beryllium copper alloy QBe2 rod at room temperature [ J]. Chinese Journal of Rare Metals, 2021, 45

(10): 1153-1161.

[8] 　魏冠义. 基于Deform 的6082 铝合金吊耳锻造工艺优化[J].热加工工艺, 2019, 48 (17): 113-116.

Wei G Y. Forging process optimization of 6082 aluminum alloy lifting lug based on Deform [J]. Hot Working Process, 2019, 48(17): 113-116.

[9] 　李志广. 连杆复合型锻造折叠缺陷分析及质量控制研究[J].模具制造, 2021, 21 (9): 56-61.

Li Z G. Research on folding defect analysis and quality control of composite forging of connecting rod [ J]. Mold Manufacturing, 2021, 21 (9): 56-61.

[10] 虞松, 赵国群, 王广春. 刚塑性有限元模拟中体积变化问题处理方法[J]. 塑性工程学报, 2003, 10 (3): 1-5.

Yu S, Zhao G Q, Wang G C. Treatment method of volume change in rigid plastic finite element simulation [J]. Journal of Plastic Engineering, 2003, 10 (3): 1-5.

[J]. 新技术新工艺, 2015, (10): 58-61.

Zhao H, Li X. Application of finite element analysis in the field of fastener plastic forming [J]. New Technology and New Process, 2015, (10): 58-61.

[12] 武欢. 基于Deform 二次开发的连杆折叠缺陷预测及优化[J]. 锻压技术, 2022, 47 (2): 12-18.

Wu H. Prediction and optimization of connecting rod folding defects based on secondary development of Deform [J]. Forging & Stamping Technology, 2022, 47 (2): 12-18.

[13] Yoon J, Jeon H, Lee J. Process design of cold forging with thick plate for seat recliner parts [J]. Materials & Design, 2013, 49: 449-455.

[14] 潘鹏. 高速列车大规格高强度高耐疲劳紧固件精密成型研究[D]. 贵州: 贵阳大学, 2020.

Pan P. Research on Precision Forming of Large Size, High Strength and High Fatigue Resistant Fasteners for High-speed Train [D]. Guiyang: Guizhou University, 2020.

[15] 崔令江, 韩飞. 塑性加工工艺学[M]. 北京: 机械工业出版社, 2007.

Cui L J, Han F. Plastic Processing Technology [M]. Beijing:China Machine Press, 2007.

[16] 方秀梅, 荆志杰, 龚毅. 基于DEFORM-3D 的2024 铝合金锻造变形过程晶粒度分析[J]. 世界有色金属, 2021, (15):120-121.

Fang X M, Jing Z J, Gong Y. Grain size analysis of 2024 aluminumalloy forging deformation process based on DEFORM-3D [J].World Nonferrous Metals, 2021, (15): 120-121.

服务与反馈：

【文章下载】【加入收藏】