Abstract:
|
The effect of isothermal forging temperature on microstructure and mechanical properties of TC21 alloy forgings was studied by isothermal forging at the strain rate of 5.5×10-4s-1,deformation of 40%.The results show that the microstructure of TC21 is sensitive to forging temperature.The microstructure consists of primary α and transition β phase and when the alloy is deformed in α+β field,the volume fraction of primary equiaxed α decreases and its size increases with elevating temperature.Typical basketweave microstructure will be obtained when forging is made at the transition temperature,and the lamellar microstructure will be obtained in the β field.The tensile strength and fracture toughness are enhanced with elevating temperature,but the tensile ductility is reduced.When forging is made at 965℃,the thinner lamellar microstructure will be obtained,which possesses a good match among strength,plasticity and fracture toughness.965℃ is recommended for isothermal forging.
|
Funds:
|
|
AuthorIntro:
|
|
Reference:
|
[1]赵永庆,曲恒磊,冯亮,等.高强高韧损伤容限型钛合金TC21的研制[J].钛工业进展,2004,21(1):22-24.
[2]郭鸿镇.合金钢与有色合金锻造[M].西安:西北工业大学出版社,1999.
[3]莫畏.钛[M].北京:冶金工业出版社,2008.
[4]Filip R,Kubiak K,Ziaja W,et al.The effect of micro-structure on the mechanical properties of two-phase titaniumalloys[J].Journal of Materials Processing Technology,2003,133:84-89.
[5]周义刚,曾卫东,俞汉清.近β锻造推翻陈旧理论发展了三态组织[J].中国工程科学,2001,5(3):61-66.
[6]Nakajma K,Teral K,Miyata T.The effect of microstruc-ture on fatigue crack propagation ofα+βtitanium alloys:In-situ observation of short fatigue crack growth[J].MaterialsScience and Engineering(A),1998,243:176-181.
[7]马少俊,吴学仁,刘建中,等.TC21钛合金的微观组织对力学性能的影响[J].航空材料学报,2006,26(5):23-25.
[8]毛彭龄.钛合金的断裂韧性[J].上海钢研,1994,(3):51-54.
[9]王晓燕,郭鸿镇,袁士翀,等.等温锻造温度对TC18钛合金组织性能的影响[J].锻压技术,2008,33(3):8-11.
[10]付艳艳,宋月清,惠松骁,等.热处理对VST55531钛合金的组织和拉伸性能的影响[J].稀有金属,2008,32(4):399-403.
[11]宋鸿武,程明,张士宏,等.具有马氏体组织的TC11合金两相区变形的组织机制及工艺优化[J].稀有金属,2008,32(4):698-704.
[12]丁平平,杨屹,Yi Qin,等.钛合金等温锻造工艺优化研究[J].锻压技术,2009,34(3):121-124.
[13]费玉环,周廉,曲恒磊,等.两相区热处理对TC21钛合金显微结构的影响[J].稀有金属材料与工程,2007,36(11):1928-1932.
|
Service:
|
【This site has not yet opened Download Service】【Add
Favorite】
|
|
|