Abstract:
|
Forging defects of mould cavity non-saturate,crack,pucker and shearing edge avulsion,etc.on the astrictive clamps and operating scissors are studied by means of appearance and metallography.The results show that bad low-temperature flowing capability of steel and no tempering at high-temperature after forging cause the forging defects.Flowing capability of steel should be increased by means of increasing forging temperature to avoiding mould cavity non-saturate,crack and pucker.Shearing edge avulsion can be removed by means of tempering at high-temperature after forging.Selecting suitable mould material to reduce the forging stress can increase the mould service life.
|